Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

3M Scotch-Weld™ Thin Instant Wood Adhesives and Surface Activator

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ Thin Instant Wood Adhesives and Surface Activator.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in the manufacture and repair of furniture, cabinets, and other wood products.Information provided by 3M
Physical Properties Metric English Comments
Viscosity >= 10 cP
>= 10 cP
Mechanical Properties Metric English Comments
Shear Strength 1.38 MPa
200 psi
Overlap, Polyurethane Finish, Adhesive Failure
1.72 MPa
250 psi
Overlap, MDF, Cohesive Failure
2.41 MPa
350 psi
Overlap, Particleboard, Substrate Failure
2.41 MPa
350 psi
Overlap, Melamine, Substrate Failure
2.76 MPa
400 psi
Overlap, Pine, Substrate/Cohesive Failure
3.45 MPa
500 psi
Overlap, Polyacrylic Finish, Cohesive Failure
4.14 MPa
600 psi
Overlap, Plywood, Cohesive Failure
5.52 MPa
800 psi
Overlap, Poplar, Substrate/Cohesive Failure
5.52 MPa
800 psi
Overlap, High Pressure Laminate, Substrate Failure
5.86 MPa
850 psi
Overlap, Maple, Substrate Failure
10.7 MPa
1550 psi
Overlap, Steel, Adhesive Failure
11.7 MPa
1700 psi
Overlap, Aluminum, Adhesive Failure
16.9 MPa
2450 psi
Overlap, Oak, Substrate/Cohesive Failure
1.03 MPa

@Temperature 66.0 °C
150 psi

@Temperature 151 °F
Overlap, Polyurethane Finish, Adhesive Failure
1.38 MPa

@Temperature 66.0 °C
200 psi

@Temperature 151 °F
Overlap, Pine, Adhesive Failure
2.07 MPa

@Temperature 32.0 °C
300 psi

@Temperature 89.6 °F
Overlap, Polyurethane Finish, 90% RH, Adhesive Failure
2.76 MPa

@Temperature 32.0 °C
400 psi

@Temperature 89.6 °F
Overlap, Pine, 90% RH, Adhesive Failure
3.10 MPa

@Temperature 32.0 °C
450 psi

@Temperature 89.6 °F
Overlap, Aluminum, 90% RH, Adhesive Failure
6.89 MPa

@Temperature 66.0 °C
1000 psi

@Temperature 151 °F
Overlap, Aluminum, Adhesive Failure
7.93 MPa

@Temperature 66.0 °C
1150 psi

@Temperature 151 °F
Overlap, Oak, Substrate/Adhesive Failure
8.27 MPa

@Temperature 66.0 °C
1200 psi

@Temperature 151 °F
Overlap, Plywood, Substrate Failure
8.62 MPa

@Temperature 32.0 °C
1250 psi

@Temperature 89.6 °F
Overlap, Oak, 90% RH, Substrate/Adhesive Failure
8.96 MPa

@Temperature 32.0 °C
1300 psi

@Temperature 89.6 °F
Overlap, Plywood, 90% RH, Substrate Failure
Processing Properties Metric English Comments
Cure Time 1440 min
24.0 hour
Full Cure
Descriptive Properties Value Comments
Appearance Clear liquid