3M Scotch-Weld™ TS230 Polyurethane Reactive Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ TS230 Polyurethane Reactive Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Sprayable/extrudable grade with long set time ideal for bonding a wide variety of plastics including polystyrene and polyacrylic. Bonds aluminum and glass to plastic and wood.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	>= 1.09 g/cc	>= 0.0394 lb/in³
Brookfield Viscosity	9000 cP	9000 cP	Thermosel using spindle #27

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	45	45
Tensile Strength at Break	22.8 MPa	3310 psi	ASTM D638 Die C
Elongation at Break	700 %	700 %	ASTM D638 Die C
Tensile Modulus	0.0372 GPa	5.40 ksi	ASMT D638 Die C
Shear Strength	2.83 MPa @Temperature 82.0 °C	410 psi @Temperature 180 °F	Overlap, Maple
	4.07 MPa @Temperature 23.0 °C	590 psi @Temperature 73.4 °F	Overlap, Polystyrene, Substrate Failure
	4.96 MPa @Temperature 82.0 °C	720 psi @Temperature 180 °F	Overlap, FRP
	6.41 MPa @Temperature 23.0 °C	930 psi @Temperature 73.4 °F	Overlap, ABS
	8.83 MPa @Temperature 23.0 °C	1280 psi @Temperature 73.4 °F	Overlap, Polyacrylic, Substrate Failure
	10.3 MPa @Temperature 23.0 °C	1490 psi @Temperature 73.4 °F	Overlap, Polycarbonate
	10.8 MPa @Temperature 23.0 °C	1570 psi @Temperature 73.4 °F	Overlap, Maple
	12.3 MPa @Temperature 23.0 °C	1780 psi @Temperature 73.4 °F	Overlap, PVC, Substrate Failure
	15.5 MPa @Temperature 23.0 °C	2250 psi @Temperature 73.4 °F	Overlap, FRP
Peel Strength	2.80 kN/m	16.0 pli	T-Peel, Initial, Substrate failure
	3.86 kN/m	22.0 pli	T-Peel, Aged 71°C for 2 weeks, Substrate failure
	8.77 kN/m	50.0 pli	180°, Polystyrene
	8.94 kN/m	51.0 pli	180°, Aluminum
	9.47 kN/m	54.0 pli	180°, Polyacrylic
	9.64 kN/m	55.0 pli	180°, ABS, Cotton duck failed during testing
	10.9 kN/m	62.0 pli	180°, Glass
	13.3 kN/m	76.0 pli	180°, PVC, Cotton duck failed during testing
	15.8 kN/m	90.0 pli	180°, FRP, Cotton duck failed during testing
	16.7 kN/m	95.0 pli	180°, Polycarbonate, Cotton duck failed during testing

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F

Processing Properties	Metric	English	Comments
Cure Time	2.50 min	0.0417 hour	Set Time