3M Scotch-Weld™ 1870 Industrial Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ 1870 Industrial Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: A fast drying, highly flexible adhesive with very long tack range and good water resistanceFor bonding fabrics and most other lightweight materials with little or no tendency to stain or bleed through.Information provided by 3M

Physical Properties	Metric	English	Comments
Solids Content	26 - 30 %	26 - 30 %
Brookfield Viscosity	450 - 1250 cP	450 - 1250 cP	RVF #3 sp @ 20 rpm @ 27°C

Mechanical Properties	Metric	English	Comments
Peel Strength	0.526 kN/m @Temperature 82.0 °C, Time 1.81e+6 sec	3.00 pli @Temperature 180 °F, Time 504 hour	180°, Canvas/Steel
	0.701 kN/m @Temperature 66.0 °C, Time 1.81e+6 sec	4.00 pli @Temperature 151 °F, Time 504 hour	180°, Canvas/Steel
	1.23 kN/m @Temperature 24.0 °C, Time 259000 sec	7.00 pli @Temperature 75.2 °F, Time 72.0 hour	180°, Canvas/Steel
	1.23 kN/m @Temperature 24.0 °C, Time 432000 sec	7.00 pli @Temperature 75.2 °F, Time 120 hour	180°, Canvas/Steel
	1.23 kN/m @Temperature 24.0 °C, Time 605000 sec	7.00 pli @Temperature 75.2 °F, Time 168 hour	180°, Canvas/Steel
	1.23 kN/m @Temperature 24.0 °C, Time 1.21e+6 sec	7.00 pli @Temperature 75.2 °F, Time 336 hour	180°, Canvas/Steel
	1.23 kN/m @Temperature 24.0 °C, Time 1.81e+6 sec	7.00 pli @Temperature 75.2 °F, Time 504 hour	180°, Canvas/Steel
	1.40 kN/m @Temperature 24.0 °C, Time 86400 sec	8.00 pli @Temperature 75.2 °F, Time 24.0 hour	180°, Canvas/Steel
	2.63 kN/m @Temperature -34.0 °C, Time 1.81e+6 sec	15.0 pli @Temperature -29.2 °F, Time 504 hour	180°, Canvas/Steel

Thermal Properties	Metric	English	Comments
Flash Point	-22.0 °C	-7.60 °F	TCC

Processing Properties	Metric	English	Comments
Shelf Life	7.00 Month	7.00 Month

Descriptive Properties	Value	Comments
Appearance	Tan
Base	SBR