3M Pronto™ CA-100 Instant Adhesive

Category	Polymer , Adhesive , Thermoset
Manufacturer	3M
Trade Name	Pronto™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Pronto™ CA-100 Instant Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

One-part, room-temperature curing adhesive that is ready-to-use without metering or mixing. Bonded parts reach handling strength in 5-10 seconds on many applications.Toughened material that provides high peel and impact strength, thermal shock resistance and improved heat resistance. Meets MIL-A-46050C Type II, Class 3. Base is ethyl. It takes assembled parts 20-70 seconds to reach a strength where further handling and processing can take place. Times will depend on surface to be bonded, temperature and humidity. Average T-Peel at 75°F (24°C) is 15 PIW. Tested per ASTM D 1876-61T.Information provided by 3M Adhesives Division.

Physical Properties	Metric	English	Comments
Viscosity	2500 - 4500 cP	2500 - 4500 cP

Mechanical Properties	Metric	English	Comments
Adhesive Bond Strength	0.655 MPa @Temperature 23.9 °C	95.0 psi @Temperature 75.0 °F	on nitrile rubber; ASTM D1002-64
	0.827 MPa @Temperature 23.9 °C	120 psi @Temperature 75.0 °F	on neoprene rubber; ASTM D1002-64
	4.10 MPa @Temperature 23.9 °C	595 psi @Temperature 75.0 °F	on ABS; ASTM D1002-64
	4.90 MPa @Temperature 23.9 °C	711 psi @Temperature 75.0 °F	on rigid PVC; ASTM D1002-64
	13.8 MPa @Temperature 23.9 °C	2000 psi @Temperature 75.0 °F	on steel; ASTM D1002-64
	20.0 MPa @Temperature 23.9 °C	2900 psi @Temperature 75.0 °F	on aluminum; ASTM D1002-64

Processing Properties	Metric	English	Comments
Processing Temperature	20.0 °C	68.0 °F