3M GM110 Gripping Material

Category Polymer , Adhesive
Manufacturer 3M
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M GM110 Gripping Material.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Gripping Material GM110 is based on 3M’s proprietary micro-replicated technology. 3M griping material GM 110 consists of a high-friction surface with a nylon knit backing that provides stretch in the cross-web direction. It can be attached to other substrates by sewing. 3M gripping material GM110 is ideally suited for applications requiring stretch, such as athletic gloves. When used alone on a single surface 3M gripping material provides a strong secure grip. Then used as a two-part system, for example on a glove and a handlebar grip, strength is maximized. As firmly as 3M gripping material holds, it releases just as easilyInformation provided by 3M
Physical Properties Metric English Comments
Thickness 838 microns
33.0 mil
without liner
Mechanical Properties Metric English Comments
Coefficient of Friction 2.3

@Pressure 0.0207 MPa
2.3

@Pressure 3.00 psi
wet, kinetic, contact area: 2.8 cm<sup>2</sup>
2.7

@Pressure 0.0207 MPa
2.7

@Pressure 3.00 psi
dry, kinetic, contact area: 2.8 cm<sup>2</sup>
Tear Strength 10.0 kN/m
57.1 pli
MD; ASTM D5734
Abrasion 0.050
0.050
H18, 500g, weight loss rate at 4000 revolutions; ASTM D3389
>= 6000
>= 6000
H18, 500g, through- revolutions weight loss; ASTM D3389
Film Tensile Strength at Break, MD 17.1 MPa
2480 psi
ASTM D5035
Film Tensile Strength at Break, TD 4.60 MPa
667 psi
ASTM D5035
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 71.0 °C
160 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Descriptive Properties Value Comments
Adhesive Carrier Nylon knit
Appearance Black or Off-white