3M Dyneon™ PVDF 60512/0000 Polyvinylidene Fluoride  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ PVDF 60512/0000 Polyvinylidene Fluoride  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyvinylidenefluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and oil and gas industry, PVDF is also gaining recognition in automotive, building, electronics, food processing equiptment, pharmaceutical equiptment and batteries. 3M™ Dyneon™ PVDF 60512/0000 offers a unique blend of properties of a PVDF copolymer and a PVDF homopolymer. PVDF 60512/0000 exhibits the mechanical strength and high temperature capability of a homopolymer with the ductility and impact resistance found in a copolymer. These products are ideal for many tubing and piping applications requiring high strength and good impact resistance.Temperature capability up to 130°CGood chemical resistance to a variety of aggressive fluids and solventsGood permeation resistanceGood weatherabilityImproved ductility and impact resistance over PVDF homopolymersSmooth surfacesInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Density 1.77 g/cc
0.0639 lb/in³
ISO 1183
Water Absorption <= 0.040 %
<= 0.040 %
24 hr @ 23°C; ISO 62 (method 1)
Linear Mold Shrinkage 0.030 cm/cm
0.030 in/in
Melt Index of Compound 1.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
3.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
3.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 38.0 MPa
5510 psi
50mm/min; ASTM D638
Tensile Strength, Yield 38.0 MPa
5510 psi
50mm/min; ASTM D638
Elongation at Break 225 %
225 %
50mm/min; ASTM D638
Elongation at Yield 11 %
11 %
50mm/min; ASTM D638
Tensile Modulus 1.30 GPa
189 ksi
1mm/min; ASTM D638
Thermal Properties Metric English Comments
Melting Point 173 °C
343 °F
ASTM D3418
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
Descriptive Properties Value Comments
Form Pellets