3M Dyneon™ PVDF 6008/0001 Polyvinylidene Fluoride

Category Polymer , Thermoplastic , Fluoropolymer , PVDF
Manufacturer 3M Dyneon™
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ PVDF 6008/0001 Polyvinylidene Fluoride.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and oil and gas industry, PVDF is also gaining recognition in automotive, building, electronics, pharmaceutical and batteries. 3M™ Dyneon™ PVDF 6008/0001 is easily processed under a variety of conventional thermoplastic conversion techniques, being particularly suitable for extrusion. PVDF 6008/0001 is inherently pure and chemically resistant against a variety of aggressive fluids and solvents. PVDF 6008/0001 exhibits excellent dimensional stability, abrasion resistance and high strength, and maintains its mechanical properties at elevated temperature.Excellent chemical resistance to a variety of aggressive fluids and solventsGood permeation resistanceSmooth, anti-fouling surfacesInjection molding gradeExcellent strength and dimensional stabilityGood color stabilityInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ISO 1183
Water Absorption <= 0.040 %
<= 0.040 %
24 hr @ 23°C; ISO 62 (method 1)
Melt Index of Compound 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
24 g/10 min

@Load 5.00 kg,
Temperature 230 °C
24 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
50mm/min; ASTM D638
Tensile Strength, Yield 42.0 MPa
6090 psi
50mm/min; ASTM D638
Elongation at Break 35 %
35 %
50mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
50mm/min; ASTM D638
Flexural Modulus 2.20 GPa
319 ksi
2mm/min; ASTM D790
Thermal Properties Metric English Comments
Melting Point 174 °C
345 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 147 °C
297 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 112 °C
234 °F
Flammability, UL94 V-0
V-0
Oxygen Index 44 %

@Thickness 3.00 mm
44 %

@Thickness 0.118 in
Sheet; ASTM D2863
Shrinkage 3.0 %
3.0 %
Descriptive Properties Value Comments
Form Pellets