3M Dyneon™ PVDF 31008/0009 Polyvinylidene Fluoride  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ PVDF 31008/0009 Polyvinylidene Fluoride  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Copolymer of VF2 and CTFEUltra-flexibleVery low shrinkage ratesWide operating temperature windowProcessable using a variety of thermoplastic conversation techniquesExcellent low flame and low smoke performanceInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ISO 1183
Water Absorption <= 0.040 %
<= 0.040 %
24 hr @ 23°C; ISO 62 (method 1)
Melt Index of Compound 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
15 g/10 min

@Load 5.00 kg,
Temperature 230 °C
15 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 22.0 MPa
3190 psi
50mm/min; ASTM D638
Elongation at Break 475 %
475 %
50mm/min; ASTM D638
Flexural Modulus 0.800 GPa
116 ksi
2mm/min; ASTM D790
Thermal Properties Metric English Comments
Melting Point 168 °C
334 °F
ASTM D3418
Brittleness Temperature -30.0 °C
-22.0 °F
ASTM D746A
Flammability, UL94 V-0
V-0
Oxygen Index >= 100 %

@Thickness 3.00 mm
>= 100 %

@Thickness 0.118 in
Sheet; ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
10 mA, after 2 min; ASTM D257
Surface Resistivity per Square >= 1.00e+14 ohm
>= 1.00e+14 ohm
< 1V after 2 min - 500 V; ASTM D257
Dielectric Constant 7.0

@Frequency 1e+6 Hz
7.0

@Frequency 1e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Form Pellets