3M Dyneon™ PFE 300Z Clear Perfluoroelastomer System

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer 3M Dyneon™
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ PFE 300Z Clear Perfluoroelastomer System.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features and Benefits:Proprietary polymer and catalyst system enables the manufacture of optically clear finished partsProportionate polymer and catalyst package simplifies the mixing processLow extractables, low outgassing, and low particle generation for ultra high purity applicationsPhosphorous-free and silica free formulation reduces the potential for contaminationExcellent temperature resistance optimizes performance in extreme environments (continuous, in-service temperatures to 300°C with peaks up to 350°C)Excellent compression set offers enhanced sealing force retention and seal lifeSmaller, easy to store units for clean room handlingInformation provided by the Dyneon division of 3M.
Physical Properties Metric English Comments
Mooney Viscosity 80

@Temperature 121 °C
 80

@Temperature 250 °F
 ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 60
60
Press Cure 10 Minutes @ 165°C (350°F) Ramp Post Cure in Air; ASTM D2240
56

@Time 86400 sec
 56

@Time 24.0 hour
 Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D2240
57

@Time 14400 sec
 57

@Time 4.00 hour
 Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D2240
Tensile Strength at Break 13.2 MPa

@Time 86400 sec
 1910 psi

@Time 24.0 hour
 Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells
13.8 MPa

@Time 14400 sec
 2000 psi

@Time 4.00 hour
 Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells
Elongation at Break 295 %
295 %
Press Cure 10 Minutes @ 165°C (350°F) Ramp Post Cure in Air; ASTM D412 Die D Dumbbells
275 %

@Time 86400 sec
 275 %

@Time 24.0 hour
 Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells
295 %

@Time 14400 sec
 295 %

@Time 4.00 hour
 Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells
100% Modulus 0.00120 GPa

@Time 86400 sec
 0.174 ksi

@Time 24.0 hour
 Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells
0.00130 GPa

@Time 14400 sec
 0.189 ksi

@Time 4.00 hour
 Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells
Compression Set 8.0 %

@Treatment Temp. 200 °C,
Time 79200 sec
 8.0 %

@Treatment Temp. 392 °F,
Time 22.0 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
15 %

@Treatment Temp. 250 °C,
Time 79200 sec
 15 %

@Treatment Temp. 482 °F,
Time 22.0 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
16 %

@Treatment Temp. 200 °C,
Time 252000 sec
 16 %

@Treatment Temp. 392 °F,
Time 70.0 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
19 %

@Treatment Temp. 250 °C,
Time 252000 sec
 19 %

@Treatment Temp. 482 °F,
Time 70.0 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
19 %

@Treatment Temp. 250 °C,
Time 252000 sec
 19 %

@Treatment Temp. 482 °F,
Time 70.0 hour
 4 hrs, Method B, -214 O-rings; ASTM D395
20 %

@Treatment Temp. 250 °C,
Time 252000 sec
 20 %

@Treatment Temp. 482 °F,
Time 70.0 hour
 4 hrs, Method B, -214 O-rings; ASTM D395
20 %

@Treatment Temp. 200 °C,
Time 605000 sec
 20 %

@Treatment Temp. 392 °F,
Time 168 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
22 %

@Treatment Temp. 250 °C,
Time 605000 sec
 22 %

@Treatment Temp. 482 °F,
Time 168 hour
 24 hrs, Method B, -214 O-rings; ASTM D395
24 %

@Treatment Temp. 250 °C,
Time 605000 sec
 24 %

@Treatment Temp. 482 °F,
Time 168 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
24 %

@Treatment Temp. 250 °C,
Time 605000 sec
 24 %

@Treatment Temp. 482 °F,
Time 168 hour
 24 hrs, Method B, -214 O-rings; ASTM D395
25 %

@Treatment Temp. 200 °C,
Time 1.21e+6 sec
 25 %

@Treatment Temp. 392 °F,
Time 336 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
26 %

@Treatment Temp. 275 °C,
Time 79200 sec
 26 %

@Treatment Temp. 527 °F,
Time 22.0 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
28 %

@Treatment Temp. 250 °C,
Time 1.21e+6 sec
 28 %

@Treatment Temp. 482 °F,
Time 336 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
33 %

@Treatment Temp. 275 °C,
Time 252000 sec
 33 %

@Treatment Temp. 527 °F,
Time 70.0 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
36 %

@Treatment Temp. 275 °C,
Time 605000 sec
 36 %

@Treatment Temp. 527 °F,
Time 168 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
53 %

@Treatment Temp. 275 °C,
Time 1.21e+6 sec
 53 %

@Treatment Temp. 527 °F,
Time 336 hour
 Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395
Optical Properties Metric English Comments
Transmission, Visible 25 %
25 %
translucent, but thickness not quantified
Component Elements Properties Metric English Comments
Fluorine, F 72.4 %
72.4 %
Processing Properties Metric English Comments
Feed Temperature 50.0 - 70.0 °C
122 - 158 °F
Die Temperature 70.0 - 90.0 °C
158 - 194 °F
Head Temperature 70.0 - 90.0 °C
158 - 194 °F
Screw Cooling Temperature 60.0 - 80.0 °C
140 - 176 °F
Descriptive Properties Value Comments
Color Translucent, Clear-Amber
Dry Heat Resistance of Vulcanizate - 100% Modulus 1.103 MPa
300°C; 336 hours
1.13 MPa
300°C; 168 hours
1.17 MPa
300°C; 70 hours
1.62 MPa
250°C; 70 hours
1.72 MPa
200°C; 168 hours
1.75 MPa
250°C; 336 hours
1.83 MPa
200°C; 70 hours
1.86 MPa
250°C; 168 hours
2.03 MPa
200°C; 336 hours
275°C; 168 hours MPa
°C; hours
275°C; 70 hours MPa
°C; hours
Dry Heat Resistance of Vulcanizate - Elongation 250 percent
275°C; 70 hours
255 percent
250°C; 168 hours
270 percent
275°C; 168 hours
275 percent
200°C; 168 hours
280 percent
200°C; 336 hours
280 percent
250°C; 70 hours
280 percent
250°C; 336 hours
290 percent
200°C; 70 hours
370 percent
300°C; 70 hours
375 percent
300°C; 168 hours
380 percent
300°C; 336 hours
Dry Heat Resistance of Vulcanizate - Shore A Hardness 55
275°C; 70 hours
55
275°C; 168 hours
56
300°C; 336 hours
57
300°C; 70 hours
57
300°C; 168 hours
60
250°C; 336 hours
60
250°C; 70 hours
61
250°C; 168 hours
63
200°C; 70 hours
64
200°C; 168 hours
65
200°C; 336 hours
Dry Heat Resistance of Vulcanizate - Tensile Strength at Break 10.89 MPa
275°C; 168 hours
11.51 MPa
300°C; 336 hours
12.89 MPa
300°C; 168 hours
12.96 MPa
275°C; 70 hours
15.2 MPa
300°C; 70 hours
16.89 MPa
250°C; 336 hours
17.72 MPa
250°C; 168 hours
18.34 MPa
200°C; 70 hours
19.51 MPa
250°C; 70 hours
19.96 MPa
200°C; 168 hours
20.86 MPa
200°C; 336 hours
Form Slab
MH, Maximum Toque 3.7 inch-lb
100 cpm, 0.5° Arc, 10 Minutes @ 165°C
ML, Minimum Torque 1.0 inch-lb
100 cpm, 0.5° Arc, 10 Minutes @ 165°C
t2, Time to 2 Inch-lb Rise from Minimum 3.2 Minute
100 cpm, 0.5° Arc, 10 Minutes @ 165°C
t'50, Time to 50% Cure 2.1 Minutes
100 cpm, 0.5° Arc, 10 Minutes @ 165°C
t'90, Time to 90% Cure 5.2 Minutes
100 cpm, 0.5° Arc, 10 Minutes @ 165°C