3M Dyneon™ PFA FLEX 8515 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules

Category Polymer , Thermoplastic , Fluoropolymer , PFA
Manufacturer 3M Dyneon™
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ PFA FLEX 8515 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Dyneon™ PFA-FLEX UHP family exhibits improved environmental stress crack resistance to stress cracking agents such as fluorsurfactants and fluorosurfactant-containing chemicals. In addition, this family offers very low levels of extractable ions, making it suitable for critical semiconductor wet chemical processes. Features and benefits includeSignificantly longer life in fluorosurfactant containing fluidsExtremely low levels of extractable ionsSmoother surfacesImproved clarityTemperature capability up to 240°CExcellent chemical resistanceInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Specific Gravity 2.145 g/cc
2.145 g/cc
ASTM D792
Water Absorption <= 0.50 %
<= 0.50 %
24 hr.; ASTM D570
Melt Index of Compound 15 g/10 min

@Load 5.00 kg,
Temperature 372 °C
15 g/10 min

@Load 11.0 lb,
Temperature 702 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 34.0 MPa
4930 psi
ASTM D638
Elongation at Break 350 %
350 %
ASTM D638
Flexural Modulus 0.600 GPa
87.0 ksi
ASTM D790
Thermal Properties Metric English Comments
Melting Point 290 °C
554 °F
ASTM D4591
Maximum Service Temperature, Air 240 °C
464 °F
Oxygen Index >= 95 %
>= 95 %
ASTM D2863
Electrical Properties Metric English Comments
Dielectric Constant 2.02 - 2.08

@Frequency 1e+6 Hz
2.02 - 2.08

@Frequency 1e+6 Hz
ASTM D150
Dissipation Factor <= 0.00030

@Frequency 1e+6 Hz
<= 0.00030

@Frequency 1e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Form Pellets