3M Dyneon™ FE 5830Q Fluoroelastomer

Category Polymer , Thermoset , Fluoropolymer, TS , Rubber or Thermoset Elastomer (TSE)
Manufacturer 3M Dyneon™
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ FE 5830Q Fluoroelastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Dyneon™ Fluoroelastomer FE 5830Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formulations. The “dry” ingredients should be blended before adding to the masticated gum. For best results, Dyneon FE 5830Q should be banded on the mill several minutes prior to adding the blended dry ingredients. Once mixed, the compounded stocks have good scorch resistance and storage stabilityComposition: Ter-polymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethyleneHighest fluorine level extrusion grade Dyneon fluoroelastomer availableProcess targets: extrusions onlyProprietary incorporated cure technologyProduces smooth extrudates without the use of processing aidsCan be formulated to meet -40°C mandrel bend fuel hose specificationsCan be formulated to yield good permeation resistance to automotive fuelsHighest fluorine level extrusion grade Dyneon fluoroelastomer availableInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Specific Gravity 1.90 g/cc
1.90 g/cc
Mooney Viscosity 33

@Temperature 121 °C
33

@Temperature 250 °F
ML1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 80
80
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D2240
Tensile Strength at Break 11.0 MPa
1600 psi
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
Elongation at Break 250 %
250 %
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
100% Modulus 0.00441 GPa
0.640 ksi
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
Compression Set 44 %
44 %
Aged 70 hours @ 200°C, -214 O-rings; ASTM D395 Method B
Thermal Properties Metric English Comments
Transformation Temperature -7.00 °C
19.4 °F
TR10; ASTM D1329
Component Elements Properties Metric English Comments
Fluorine, F 70.5 %
70.5 %
Descriptive Properties Value Comments
Color Opaque Off-White
MH, Maximum Torque 14.5 inch-lb
100 cpm, 0.5° Arc, 6 Minutes @ 177°C
ML, Minimum Torque 1 inch-lb
100 cpm, 0.5° Arc, 6 Minutes @ 177°C
Solubility Ketones and Esters
t`50, Time to 50% cure 2.3 minutes
100 cpm, 0.5° Arc, 6 Minutes @ 177°C
t`90 - Time to 90% cure 3.3 minutes
100 cpm, 0.5° Arc, 6 Minutes @ 177°C
ts2 - Time to 2 in-lb rise from min 2 minutes
100 cpm, 0.5° Arc, 6 Minutes @ 177°C