3M 7881 Computer-Imprintable Polyester Label Material

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M 7881 Computer-Imprintable Polyester Label Material.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features:Topcoated polyester is compatible with dot matrix printing and is hand writeable. The matte coating resists degradation from scuffing, chemicals, moisture, and wide temperature fluctuations. The topcoat also provides improved ink anchorage for traditional forms of press printing.#300 adhesive bonds well to a wide variety of substrates including metals, high surface energy (HSE) plastics and low surface energy (LSE) plastics. It is ideal for applications requiring high initial adhesion especially to LSE plastic surfaces.55# densified kraft liner assures consistent die cutting.3M™ Label Material 7881 is UL recognized (Files MH11410) and CSA accepted (File 99316). See the UL and CSA listings for detailsApplications:Barcode labels and rating plates.Property identification and asset labeling.Warning, instruction, and service labels for durable goods.Nameplates for durable goods.Information provided by 3M

Physical Properties	Metric	English	Comments
Thickness	20.3 microns	0.800 mil	Adhesive
	58.4 microns	2.30 mil	Facestock
	81.3 microns	3.20 mil	Liner

Mechanical Properties	Metric	English	Comments
Peel Strength	0.09861 kN/m	0.5625 pli	LD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.110 kN/m	0.625 pli	LD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.18626 kN/m	1.0625 pli	Polycarbonate 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.27391 kN/m	1.5625 pli	LD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.307 kN/m	1.75 pli	HD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.307 kN/m	1.75 pli	HD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.31773 kN/m	1.8125 pli	HD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.3287 kN/m	1.875 pli	Polycarbonate 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.3287 kN/m	1.875 pli	LD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.351 kN/m	2.00 pli	LD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.351 kN/m	2.00 pli	HD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.3725 kN/m	2.125 pli	LD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.38347 kN/m	2.1875 pli	HD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.394 kN/m	2.25 pli	LD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.394 kN/m	2.25 pli	Polycarbonate 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.4163 kN/m	2.375 pli	Polypropylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.4163 kN/m	2.375 pli	Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.438 kN/m	2.50 pli	HD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.438 kN/m	2.50 pli	HD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.4602 kN/m	2.625 pli	Stainless Steel, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.4602 kN/m	2.625 pli	Glass, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.4602 kN/m	2.625 pli	LD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.4602 kN/m	2.625 pli	Polypropylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.482 kN/m	2.75 pli	Polycarbonate 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.482 kN/m	2.75 pli	Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.482 kN/m	2.75 pli	Glass, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.49303 kN/m	2.8125 pli	HD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.5040 kN/m	2.875 pli	Stainless Steel, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.5040 kN/m	2.875 pli	Polycarbonate 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.526 kN/m	3.00 pli	Glass, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.5478 kN/m	3.125 pli	Stainless Steel, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.5478 kN/m	3.125 pli	Glass, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.58068 kN/m	3.3125 pli	Polypropylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.58068 kN/m	3.3125 pli	Stainless Steel, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.5916 kN/m	3.375 pli	Polypropylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.60259 kN/m	3.4375 pli	Polycarbonate 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.614 kN/m	3.50 pli	Stainless Steel, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.614 kN/m	3.50 pli	Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.64642 kN/m	3.6875 pli	Polycarbonate 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.657 kN/m	3.75 pli	Glass, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
	0.66833 kN/m	3.8125 pli	Polycarbonate 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.7231 kN/m	4.125 pli	Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.73407 kN/m	4.1875 pli	Glass, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.73407 kN/m	4.1875 pli	Stainless Steel, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
	0.745 kN/m	4.25 pli	Stainless Steel, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
	0.7669 kN/m	4.375 pli	Stainless Steel, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.7669 kN/m	4.375 pli	Glass, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
	0.77789 kN/m	4.4375 pli	Glass, 180° Peel, Conditioned for 3 days at RT; ASTM D3330

Processing Properties	Metric	English	Comments
Shelf Life	24.0 Month	24.0 Month

Descriptive Properties	Value	Comments
Adhesive Carrier	55# Densified kraft
Adhesive Type	#300 Acrylic