3M 7745FL Polyester Overlaminating Film

Category Polymer , Adhesive
Manufacturer 3M
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M 7745FL Polyester Overlaminating Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Polyester Overlaminating Film 7745FL utilizes a matte clear polyester that is recommended for optimum durability and appearance in dot matrix and hand writable applications. The matte coating resists degradation from scuffing, chemicals, moisture, and wide temperature fluctuations. 3M™ Adhesive 400 offers excellent low temperature performance and long term aging for resistance to yellowing in outdoor applications.Information provided by 3M
Physical Properties Metric English Comments
Thickness 20.3 microns
0.800 mil
Adhesive
33.0 microns
1.30 mil
Facestock
38.1 microns
1.50 mil
Liner
Mechanical Properties Metric English Comments
Peel Strength 0.05478 kN/m
0.3125 pli
LD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.07669 kN/m
0.4375 pli
LD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.0877 kN/m
0.500 pli
HD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.09861 kN/m
0.5625 pli
LD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.110 kN/m
0.625 pli
LD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.1205 kN/m
0.6875 pli
LD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.131 kN/m
0.750 pli
HD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.131 kN/m
0.750 pli
HD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
0.153 kN/m
0.875 pli
HD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
0.153 kN/m
0.875 pli
LD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
0.153 kN/m
0.875 pli
HD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.1643 kN/m
0.9375 pli
HD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.1643 kN/m
0.9375 pli
HD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.18626 kN/m
1.0625 pli
LD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
0.18626 kN/m
1.0625 pli
LD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.20817 kN/m
1.1875 pli
Polypropylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.23008 kN/m
1.3125 pli
HD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.23008 kN/m
1.3125 pli
Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.25199 kN/m
1.4375 pli
Stainless Steel, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.263 kN/m
1.50 pli
Glass, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.27391 kN/m
1.5625 pli
Polypropylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.2849 kN/m
1.625 pli
Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
0.2849 kN/m
1.625 pli
Polycarbonate 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.2849 kN/m
1.625 pli
Glass, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.29582 kN/m
1.6875 pli
Polypropylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.29582 kN/m
1.6875 pli
Polycarbonate 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.307 kN/m
1.75 pli
Polycarbonate 90° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.307 kN/m
1.75 pli
Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.31773 kN/m
1.8125 pli
Stainless Steel, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.31773 kN/m
1.8125 pli
Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
0.351 kN/m
2.00 pli
Glass, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.351 kN/m
2.00 pli
Stainless Steel, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
0.351 kN/m
2.00 pli
Polypropylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.36156 kN/m
2.0625 pli
Stainless Steel, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.36156 kN/m
2.0625 pli
Polycarbonate 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.36156 kN/m
2.0625 pli
Polycarbonate 180° Peel, Initial, 10 min dwell at RT; ASTM D3330
0.3725 kN/m
2.125 pli
Polycarbonate 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.40538 kN/m
2.3125 pli
Polycarbonate 90° Peel, Conditioned for 3 days at RT; ASTM D3330
0.4163 kN/m
2.375 pli
Stainless Steel, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.4163 kN/m
2.375 pli
Glass, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.42729 kN/m
2.4375 pli
Polycarbonate 180° Peel, Conditioned for 3 days at RT; ASTM D3330
0.438 kN/m
2.50 pli
Glass, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
0.438 kN/m
2.50 pli
Glass, 90° Peel, Conditioned for 3 days at RT; ASTM D3330
0.44921 kN/m
2.5625 pli
Stainless Steel, 180° Peel, Conditioned for 3 days at RT; ASTM D3330
0.5040 kN/m
2.875 pli
Stainless Steel, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.51494 kN/m
2.9375 pli
Glass, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
0.5478 kN/m
3.125 pli
Glass, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330
0.73407 kN/m
4.1875 pli
Stainless Steel, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Service
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Service
-12.0 °C
10.4 °F
Application
Processing Properties Metric English Comments
Shelf Life 24.0 Month
24.0 Month
Descriptive Properties Value Comments
Adhesive Type #400 Acrylic
Liner Clear Polyester Liner