| Peel Strength |
0.1205 kN/m |
0.6875 pli |
Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.1643 kN/m |
0.9375 pli |
Polypropylene, 90° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.1643 kN/m |
0.9375 pli |
LD Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.3287 kN/m |
1.875 pli |
Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.33964 kN/m |
1.9375 pli |
HD Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.33964 kN/m |
1.9375 pli |
LD Polypropylene, 90° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.33964 kN/m |
1.9375 pli |
HD Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.33964 kN/m |
1.9375 pli |
LD Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.351 kN/m |
2.00 pli |
HD Polypropylene, 90° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.58068 kN/m |
3.3125 pli |
LD Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.6355 kN/m |
3.625 pli |
LD Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.657 kN/m |
3.75 pli |
HD Polypropylene, 180° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.657 kN/m |
3.75 pli |
HD Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.701 kN/m |
4.00 pli |
LD Polypropylene, 180° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.73407 kN/m |
4.1875 pli |
HD Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.77789 kN/m |
4.4375 pli |
Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.82172 kN/m |
4.6875 pli |
Polypropylene, 180° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.84363 kN/m |
4.8125 pli |
Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |