3M 4000 UV 6580 Marine Adhesive/Sealant Fast Cure

Category Polymer , Adhesive
Manufacturer 3M
Trade Name 4000 UV
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M 4000 UV 6580 Marine Adhesive/Sealant Fast Cure.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Marine Adhesive/Sealant 4000 UV is a one-part adhesive sealant that cures to form a firm, rubbery waterproof seal. Its flexibility allows for the dissipation of stress caused by shock, vibration, swelling or shrinking. Designed for marine applications above and below the waterline. Its superior UV resistance properties makes this an ideal cosmetic adhesive sealant.Features:Superior UV resistance. Non-corrosive. Exceptional sealing properties. Non-cracking.< 1% VOC’s Caulkable at low temperatures (>40°F [4°C]). Low odor. Fast curing.Non-shrinking. Paintable (test for suitability).Non-sagging.Information provided by 3M
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Mechanical Properties Metric English Comments
Hardness, Shore A 38 - 39
38 - 39
Tensile Strength at Break 1.74 MPa
252 psi
50% RH
2.06 MPa

@Time 3.60e+6 sec
299 psi

@Time 1000 hour
G-26, B, BH; ASTM D412
2.11 MPa

@Time 1.80e+6 sec
306 psi

@Time 500 hour
G-26, B, BH; ASTM D412
Elongation at Break 790 %
790 %
50% RH
723 %

@Time 3.60e+6 sec
723 %

@Time 1000 hour
G-26, B, BH; ASTM D412
804 %

@Time 1.80e+6 sec
804 %

@Time 500 hour
G-26, B, BH; ASTM D412
Shear Strength 1.20 MPa
174 psi
Overlap, Teak, 50% RH
1.35 MPa
196 psi
Overlap, Teak (primed), 50% RH
1.56 MPa
226 psi
Overlap, Fir, 50% RH
1.73 MPa
251 psi
Overlap, Fiberglass, 50% RH
1.92 MPa
279 psi
Overlap, ABS, 50% RH
2.27 MPa
329 psi
Overlap, Aluminum, 50% RH
2.92 MPa
424 psi
Overlap, Gelcoat, 50% RH
0.931 MPa

@Time 1.80e+6 sec
135 psi

@Time 500 hour
Overlap, Nylon, 50% RH, Salt Water Immersion
1.96 MPa

@Time 1.80e+6 sec
284 psi

@Time 500 hour
Overlap, Fiberglass, 50% RH, Salt Water Immersion
2.48 MPa

@Time 1.80e+6 sec
359 psi

@Time 500 hour
Overlap, Gelcoat, 50% RH, Salt Water Immersion
2.63 MPa

@Time 1.80e+6 sec
381 psi

@Time 500 hour
Overlap, Aluminum, 50% RH, Salt Water Immersion
3.28 MPa

@Time 1.80e+6 sec
475 psi

@Time 500 hour
Overlap, Copper, 50% RH, Salt Water Immersion
3.74 MPa

@Time 1.80e+6 sec
542 psi

@Time 500 hour
Overlap, Bronz, 50% RH, Salt Water Immersion
4.65 MPa

@Time 1.80e+6 sec
675 psi

@Time 500 hour
Overlap, Stainless Steel, 50% RH, Salt Water Immersion
Peel Strength 0.929 kN/m
5.30 pli
180°, Aluminum, 50% RH
1.40 kN/m
8.00 pli
180°, Teak (primed), 50% RH
1.44 kN/m
8.20 pli
180°, Fiberglass, 50% RH
1.53 kN/m
8.70 pli
180°, Teak, 50% RH
1.54 kN/m
8.80 pli
180°, Gelcoat, 50% RH
1.65 kN/m
9.40 pli
180°, Mahogany, 50% RH
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 90.0 °C
194 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Processing Properties Metric English Comments
Cure Time 22.0 min
0.367 hour
Tack-Free, 50% RH
1440 min
24.0 hour
Full Cure, 50% RH
Shelf Life 12.0 Month
12.0 Month
in the original, unopened container