Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group DECAL® 1760 Phenolic Glass-fiber reinforced phenolic molding compound. Very good electrical properties, good chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals an.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group DECAL® 2061 Phenolic Wood flour reinforced phenolic molding compound. Good electrical properties, chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and .. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group DECAL® 5431 Phenolic Organically and inorganically filled phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group DECAL® 572R Phenolic Glass-fiber reinforced phenolic molding compound. Exceptional heat resistance with regard to maintaining surface finish and mechanical properties, outstanding mechanical properties, excellent rotati.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group DECAL® 937 Phenolic Mica reinforced phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (W.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group EN 5007 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group EPOXIDUR® 3582 EP Epoxy Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Moldi.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group EPOXIDUR® 3585 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures, excel.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group MELOPAS® 156 MF Melamine Glass fiber reinforced Melamine molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 200.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm @Thickness 1.00 mm |
508 - 762 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60250 |
Raschig Group RALUPOL® 2200 UP Polyester Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets.. |
|||
Dielectric Strength | 15.7 - 30.0 kV/mm | 400 - 762 kV/in | Average value: 20.1 kV/mm Grade Count:13 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | IEC 60243-1 |
Raschig Group RESINOL® 87120 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets .. |
|||
Dielectric Strength | 15.0 - 30.0 kV/mm | 381 - 762 kV/in | Average value: 21.6 kV/mm Grade Count:26 |
Overview of materials for Nylon 46, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | Average value: 26.2 kV/mm Grade Count:3 |
Overview of materials for Nylon 11, Cable Sheathing Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11, Cable Sheathing Grade". Each property range of values reported is minimum and maximum values o.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm @Thickness 2.00 mm |
508 - 762 kV/in @Thickness 0.0787 in |
IEC 60243 |
Manifattura Cattaneo PVDF Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | DIN 53481 |
Isoflon PA 12 Polyamide 12 General use for mechanical partsGood heat resistanceEasy to useInformation provided by Isoflon. |
|||
Dielectric Strength | 28.0 - 30.0 kV/mm | 711 - 762 kV/in | DIN 53481 |
Isoflon PC Polycarbonate Good impact resistance among transparent materialsInformation provided by Isoflon. |
|||
Dielectric Strength | 25.0 - 30.0 kV/mm | 635 - 762 kV/in | DIN 53481 |
Isoflon PEEK Polyetheretherketone Materials with strong mechanical and electrical performances under high temperatures.Information provided by Isoflon. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | ASTM D149 |
Guarniflon FEP Fluorinated Ethylene Propylene Fluorinated thermoplastic material with excellent thermal, electrical and chemical inertness properties. Widely used for different industrial applications for its excellent chemical resistance up t.. |
|||
Dielectric Strength | 28.0 - 30.0 kV/mm | 711 - 762 kV/in | Breakdown; DIN 53 481, IEC-243, VDE 0303 Part 1 |
Hippe PA 66 Nylon 66 The polyamide with high degree of hardness, stiffness, scuff strength and stability of shape under heat. Preferred polyamide for components subjected to high load and heat stress in electrical, mec.. |
|||
Dielectric Strength | 25.0 - 30.0 kV/mm | 635 - 762 kV/in | DC Breakdown Strength |
China-Yixing Longly Refractories 75 Alumina Ceramic LONGLY selects high quality ceramic fine powder and micropowder as materials, adopts modern advanced molding technology to produce a multitude of ceramic tubes, rods, beads, balls, columns, plates, .. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | Average value: 22.1 kV/mm Grade Count:19 |
Overview of materials for Polyether Ester Elastomer This property data is a summary of similar materials in the MatWeb database for the category "Polyether Ester Elastomer". Each property range of values reported is minimum and maximum values of appr.. |
|||
Dielectric Strength | 17.0 - 30.0 kV/mm | 432 - 762 kV/in | Average value: 26.8 kV/mm Grade Count:4 |
Overview of materials for Acrylic, Cast This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | DIN 53481 |
Isoflon PA 11 Polyamide 11 General use for mechanical partsGood heat resistanceEasy to useInformation provided by Isoflon. |
|||
Dielectric Strength | 4.80 - 30.0 kV/mm | 122 - 762 kV/in | Average value: 12.3 kV/mm Grade Count:21 |
Overview of materials for Melamine-Phenolic Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Melamine-Phenolic Copolymer". Each property range of values reported is minimum and maximum values of ap.. |
|||
Dielectric Strength | 9.17 - 30.0 kV/mm | 233 - 762 kV/in | Average value: 19.8 kV/mm Grade Count:49 |
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS)- 40% Glass filled; Molded". Specific grades with glass content between 35% a.. |
|||
Dielectric Strength | 19.7 - 30.0 kV/mm | 500 - 762 kV/in | Average value: 22.5 kV/mm Grade Count:15 |
Overview of materials for Polypropylene, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum .. |