Polymer Property : Dielectric Strength = 24.4 kV/mm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Dielectric Strength	24.4 kV/mm	620 kV/in	in air; ASTM D149
Polymer Resources PEI-G30 Polyetherimide, 30% Glass Reinforced Polyetherimide, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Poly..
Dielectric Strength	24.4 kV/mm	620 kV/in	Z Direction; IPC-TM-650 2.5.6.2
Rogers Corporation LoPro™ RO4730 Antenna Grade Non-PTFE Laminate RO4730 LoPro Antenna Grade Laminates are fully compatible with conventional FR-4 and high temperature lead-free solder processing. The resin systems of RO4730 dielectric materials are designed to p..
Dielectric Strength	24.4 kV/mm	620 kV/in	ASTM D149-93
Saint-Gobain TygonÂ® SE-200 Inert Tubing Formulation Description: TygonÂ® SE-200: Without sacrificing the flexibility, glass-like clarity or outstanding bend radius for which TygonÂ® tubing is known, TygonÂ® Inert Tubing can handle many applic..
Dielectric Strength	24.4 kV/mm	620 kV/in	50% RH
Cytec Cyply® 1002 Epoxy Fiberglass Composite, Isotropic CYPLY® 1002 is a cured epoxy composite material based on a unique non-woven parallel filament construction. This type of construction minimizes filament stress abrasion that can shorten fatigue li..
Dielectric Strength	24.4 kV/mm	620 kV/in	50% RH
Cytec Cyply® 1002 Epoxy Fiberglass Composite, Unidirectional CYPLY® 1002 is a cured epoxy composite material based on a unique non-woven parallel filament construction. This type of construction minimizes filament stress abrasion that can shorten fatigue li..
Dielectric Strength	24.4 kV/mm	620 kV/in	50% RH
Cytec Cyply® 1002 Epoxy Fiberglass Composite, Crossply CYPLY® 1002 is a cured epoxy composite material based on a unique non-woven parallel filament construction. This type of construction minimizes filament stress abrasion that can shorten fatigue li..