Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.000118 ohm-cm @Temperature 649 °C |
0.000118 ohm-cm @Temperature 1200 °F |
|
H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy MP35N is a nickel-cobalt based alloy of the Multiphase® alloy system that has ultra high strength, toughness, ductility, biocompatibility, and outstanding corrosion resistance. H.C. Starck offers.. |
|||
Electrical Resistivity | 0.000118 ohm-cm @Temperature 25.0 °C |
0.000118 ohm-cm @Temperature 77.0 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Electrical Resistivity | 0.000118 ohm-cm @Temperature 25.0 °C |
0.000118 ohm-cm @Temperature 77.0 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Electrical Resistivity | 0.000118 ohm-cm @Temperature 25.0 °C |
0.000118 ohm-cm @Temperature 77.0 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Electrical Resistivity | 0.000118 ohm-cm @Temperature 25.0 °C |
0.000118 ohm-cm @Temperature 77.0 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Electrical Resistivity | 0.000118 ohm-cm @Temperature 204 °C |
0.000118 ohm-cm @Temperature 400 °F |
|
Carlson C 825 Nickel-Iron-Chromium Alloy General DescriptionCarlson Alloy C 825 is a nickel-iron-chromium alloy, developed for use in extremely corrosive environments. The nickel content of this alloy makes it resistant to chloride-ion st.. |
|||
Electrical Resistivity | 0.000118 ohm-cm @Temperature 25.0 °C |
0.000118 ohm-cm @Temperature 77.0 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
Electrical Resistivity | 0.000118 ohm-cm @Temperature 25.0 °C |
0.000118 ohm-cm @Temperature 77.0 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
Electrical Resistivity | 0.000118 ohm-cm @Temperature 427 °C |
0.000118 ohm-cm @Temperature 801 °F |
|
ATI Allegheny Ludlum ALFA-I™ Stainless Steel Type 406 Characteristics:superior oxidation resistance for the temperature range 1600°F-over 2200°F, high electrical resistivity, high resistance to sulfidation, high resistance to carburization. Applicat.. |
|||
Electrical Resistivity | 0.000118 ohm-cm @Temperature 25.0 °C |
0.000118 ohm-cm @Temperature 77.0 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |