Polymer Property : Electrical Resistivity = 0.000126 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Electrical Properties Metric English Comments
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, weld metal as welded
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 600 °C
0.000126 ohm-cm

@Temperature 1110 °F
Haynes 263® alloy, cold rolled sheet, solution treated and aged
Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 700 °C
0.000126 ohm-cm

@Temperature 1290 °F
Haynes 263® alloy, cold rolled sheet, solution treated and aged
Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle..
Electrical Resistivity 0.000126 ohm-cm
0.000126 ohm-cm
Special Metals NIMONIC® Alloy PK33
A nickel-chromium-cobalt alloy that is precipitation hardenable and also contains a relatively high (7%) level of molybdenum for solid-solution strengthening. It has an exceptional combination of h..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Electrical Resistivity 0.000126 ohm-cm
0.000126 ohm-cm
Temperature Factor is 1.10 at 800°C (1470°F). Temperature Factor is 1.11 at 1000°C (1830°F).
Resistalloy International Fecralloy™ 134 Electrical Resistance Steel
Ferritic stainless steel with aluminum. Available as wire and strip. Used mainly for electrical elements in both industrial and domestic applications. Industrial applications vary from small labora..
Electrical Resistivity 0.000126 ohm-cm
0.000126 ohm-cm
ATI Wah Chang TI-3Al-2.5V
Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working an..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Electrical Resistivity 0.000126 ohm-cm

@Temperature 705 °C
0.000126 ohm-cm

@Temperature 1300 °F
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..