| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 500 °C |
0.000124 ohm-cm @Temperature 932 °F |
|
| Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 900 °C |
0.000124 ohm-cm @Temperature 1650 °F |
|
| Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 1000 °C |
0.000124 ohm-cm @Temperature 1830 °F |
|
| Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm | 0.000124 ohm-cm | |
| Special Metals NIMONIC® Alloy 80A A nickel-chromium alloy similar to NIMONIC alloy 75 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good corrosion and oxidation resistance and high tensile a.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm | 0.000124 ohm-cm | |
| Goodfellow Iron 77.5/Boron 15/Silicon 7.5 Alloy Metallic glasses (glassy alloys) or amorphous metals. Uses include soft magnetic applications, brazing, coating and as reinforcing fibers.Information provided by Goodfellow. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Electrical Resistivity | 0.000124 ohm-cm @Temperature 815 °C |
0.000124 ohm-cm @Temperature 1500 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||