Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy sheet Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 10% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 20% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 40% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 50% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 30% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Electrical Resistivity | 0.0001219 ohm-cm @Temperature 1150 °C |
0.0001219 ohm-cm @Temperature 2100 °F |
|
Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |