Polymer Property : Electrical Resistivity = 0.0000950 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 20.0 °C
0.0000950 ohm-cm

@Temperature 68.0 °F
Industeel NUCL 18.10 B4 Natural Boron (Min 1% wt) Alloyed 304 Stainless Steel
Description: Isotope B10 has the property to capture neutrons produced by nuclear reactions. Natural boron contains about 19.9 at% or 18.45 wt % of B10 isotope, the remaining being B11 isotope. NUCL..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 20.0 °C
0.0000950 ohm-cm

@Temperature 68.0 °F
Industeel SIRIUS 314 25% Cr - 1.8% Si Heat Resistant Stainless Steel
Description: CLI SIRIUS 314 grade is a fully austenitic stainless steel containing 25% Cr, 20% Ni and 1.8% Si. The alloy is designed for high temperature corrosion resistance applications even in se..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 20.0 °C
0.0000950 ohm-cm

@Temperature 68.0 °F
Industeel URANUS® B26 6 Mo High Performance Super-Austenitic Stainless Steel with PREN = 43
Description: URANUS® B26 (UR B26) is a 25% Ni, 20% Cr, 6% Mo superaustenitic stainless steel grade with 0.2 % nitrogen additions, particularly designed for high structural stability and high corr..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, cold worked sheet, 10% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, cold worked sheet, 15 % cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 25% cold reduction, 1175°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, sheet
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Electrical Resistivity 0.0000950 - 0.000105 ohm-cm
0.0000950 - 0.000105 ohm-cm
AK Steel 18 SR® Ferritic Stainless steel
AK Steel 18 SR® provides excellent resistance to high temperature scaling - far superior to that of Type 446 stainless steel. This material is readily welded by conventional methods. It is not su..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 0% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 10% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 15% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 20.0 °C
0.0000950 ohm-cm

@Temperature 68.0 °F
Industeel UREA 25.22.2 Plants
Description: CLI UREA 25.22.2 chemical composition has been optimized for specific uses in Urea plants. It is a 310L modified austenitic stainless steel with low carbon, low silicon and high nitroge..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Electrical Resistivity 0.0000950 ohm-cm

@Temperature 1000 °C
0.0000950 ohm-cm

@Temperature 1830 °F
Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..