Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 240 min | 4.00 hour | On steel (fixture) |
ND Industries 460 Instant High Pressure Pipe Sealant High temperature, high strength general purpose stainless steel and other inert metals. For metal fittings |
|||
Cure Time | 240 min @Temperature 65.6 °C |
4.00 hour @Temperature 150 °F |
98% cure |
Reltek BONDiT™ B-45 Adhesive, Sealant & Coating System Key Properties: Excellent adhesive for low surface energy plastics without primer.Used in potting, painting and protective coating applications.Excellent thermal and mechanical shock resistance.Ease.. |
|||
Cure Time | 240 min @Temperature 93.3 °C |
4.00 hour @Temperature 200 °F |
98% cure |
Reltek BONDiT™ B-46 Adhesive, Sealant & Coating System Key Properties: Excellent adhesion to low surface energy plastics without primer or surface preparation.Applications: Very high flexibility, 500% elongation, emphasizing high tack for un-abraded sub.. |
|||
Cure Time | 240 min | 4.00 hour | Full cure |
Resinlab® CYNERGY CA6303 Adhesive Description: The CYNERGY 6300 SERIES products are for use in applications where a faster set time is desired or low moisture conditions exist. Provides good bonds to a wide variety of materials.Appl.. |
|||
Cure Time | 240 min @Temperature 200 °C |
4.00 hour @Temperature 392 °F |
Post |
Shin-Etsu Silicones KE-9510U Silicone Elastomer KE9510 U is one of a series of easy processing, general purpose silicone rubber base with low volatile content. It can be used in a variety of applications requiring finishing by molding, extruding .. |
|||
Cure Time | 240 min @Temperature 200 °C |
4.00 hour @Temperature 392 °F |
Post |
Shin-Etsu Silicones KE-971U Silicone Elastomer KE971 U is one of a series of easy processing, general purpose silicone rubber bases. It can be used in a variety of applications requiring finishing by molding (compression, injection, transfer).Pr.. |
|||
Cure Time | 240 min @Temperature 200 °C |
4.00 hour @Temperature 392 °F |
Post Cure |
Shin-Etsu Silicones KEG-2000-30A/B Elastomer KEG-2000-30 is a liquid injection molding silicone. It is supplied as two components which are mixed in a 1:1 ratio to ensure easy and accurate blending. It's viscosity is low enough to allow easy.. |
|||
Cure Time | 240 min @Temperature 200 °C |
4.00 hour @Temperature 392 °F |
Post |
Shin-Etsu Silicones KE-931U Silicone Elastomer KE931 U is one of a series of easy processing, general purpose silicone rubber bases. It can be used in a variety of applications requiring finishing by molding (compression, injection, transfer).Pr.. |
|||
Cure Time | 240 - 1440 min | 4.00 - 24.0 hour | Full Cure Time @ 20ºC |
Loctite® Output™ 315 Acrylic Adhesive Thermally Conductive BondersLoctite® Thermally Conductive Adhesives eliminate the need for mechanical fasteners and clips, while providing the most efficient thermal transfer between transistors or.. |
|||
Cure Time | 240 - 360 min @Temperature 121 °C |
4.00 - 6.00 hour @Temperature 250 °F |
|
Cotronics Duralco™ 4703 Adhesive and Tooling Compound High temperature resin reinforced with ceramic and metallic fibers and particles, resulting in high thermal stability. Easily machined to close tolerances and will repair and rebuild worn or cracke.. |
|||
Cure Time | 240 min @Temperature 204 °C |
4.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
Arlon 55576R060 0.060" Cured/Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Style 162 FiberglassSide 2: Uncured Silicone RubberInterleave: 3 mil PEThis data represents typical values for the production material .. |
|||
Cure Time | 240 min | 4.00 hour | Tack-Free Time |
3M AC-251 Black Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai.. |
|||
Cure Time | 240 min | 4.00 hour | |
3M AC-251 Gray Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-251 Gray Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate air.. |
|||
Cure Time | 240 - 360 min | 4.00 - 6.00 hour | Tack Free Time, catalyzed with QM CAT 140 |
ACC QM 140 QSI Quantum Silicones 40 Durometer Condensation Cured Moldmaking Material QM 140 is a two-component, room temperature condensation cure silicone material. The cured rubber has excellent mechanical properties and good shelf-life stability. This material is an excellent cho.. |
|||
Cure Time | 240 min | 4.00 hour | Hard Dry |
3M Scotchkote™ FG 514 Urethane Ceramic Lining Scotchkote Urethane Ceramic Lining FG 514 has been specifically developed as a 100% solids polyceramic coating with a degree of flexibility for lining and resurfacing equipment operating in fluid fl.. |
|||
Cure Time | 240 min | 4.00 hour | Time to Handling Strength |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Cure Time | 240 min | 4.00 hour | 2 hrs at 160°F; 2 hrs at 300°F (Recommended Cure) |
Aremco Aremco-Bond™ 2315 High Performance Epoxide High Temperature, Low Viscosity, Potting Compound for Electrical Applications. |
|||
Cure Time | 240 min | 4.00 hour | Tack-Free Time |
3M AC-730 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca.. |
|||
Cure Time | 240 - 1440 min | 4.00 - 24.0 hour | Full Cure Time @ 20ºC |
Loctite® Output™ 383 Acrylic Adhesive Acrylic Bonding Adhesives and Thermally Conductive BondersLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impa.. |