- Polymer Property : Cure Time = 3.00 min
Polymer Property : Cure Time = 3.00 min Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C |
0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F |
|
| Quantum Composites AMC™ 8595 55% Carbon Fiber Reinforced Vinyl Ester SMC AMC™ 8595 is a vinyl ester engineered structural composite molding compound with continuous, unidirectional carbon fibers. It is designed for compression molding of components requiring high struc.. |
|||
| Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C |
0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F |
|
| Quantum Composites QC-8700 63% Glass Fiber Reinforced Vinyl Ester SMC QC-8700 is a vinyl ester engineered structural composite molding compound for compression molding of components requiring high structural strength. It exhibits unusual toughness, and is suggested f.. |
|||
| Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 149 °C |
0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 300 °F |
|
| Quantum Composites QC-8777 41% Glass Fiber Reinforced Polyester Hybrid SMC QC-8777 is a polyester hybrid engineered structural composite molding compound designed for compression molding of components requiring high structural strength, corrosion resistance and temperature.. |
|||
| Cure Time | 3.00 min | 0.0500 hour | |
| Resin Technology Group 405 Oxy-Bond™ Electrically Conductive Epoxy Adhesive Oxy-Bond and Millenium Adhesive SystemsEngineered for strength, durability, lightness, and formability, our Oxy-Bond and Millenium lines offer adhesives with physical and electrical properties to ma.. |
|||
| Cure Time | <= 3.00 min | <= 0.0500 hour | Induction |
| Permabond ES558 Epoxy Resin PERMABOND ES558 is a single-part epoxy paste which flows like solder when heated during curing. The adhesive is toughened for maximum impact resistance, along with excellent peel and shear strength... |
|||
| Cure Time | <= 3.00 min | <= 0.0500 hour | Induction |
| Permabond ES578 Epoxy Resin PERMABOND® ES578 is a single-part heat cured epoxy adhesive with excellent adhesion to metal surfaces, ceramics as well as composite materials. ES578 provides excellent thermal conductivity and bon.. |
|||
| Cure Time | <= 3.00 min | <= 0.0500 hour | Induction |
| Permabond ES569 Epoxy Resin PERMABOND® ES569 is a single-part heat cured epoxy adhesive with excellent adhesion to metal surfaces as well as composite materials. The high bond strength of this adhesive allows it to replace me.. |
|||
| Cure Time | 3.00 - 18000 min | 0.0500 - 300 hour | Average value: 1480 min Grade Count:90 |
| Overview of materials for Epoxy Encapsulant, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Encapsulant, Unreinforced". Each property range of values reported is minimum and maximum values o.. |
|||
| Cure Time | 3.00 - 4.00 min | 0.0500 - 0.0667 hour | Working time |
| ITW Devcon Flex Bondâ„¢ Methacrylate Adhesive Pipe Sealant, Purple Information provided by ITW Devcon |
|||
| Cure Time | 3.00 min @Temperature 88.0 °C |
0.0500 hour @Temperature 190 °F |
|
| Lord Adhesives Chemlok® 144 Primer LORD Chemlok® 144 primer is a one-coat, moisturecure primer used to prime and/or bond a variety of polar substrates. These substrates include steel, aluminum, brass, e-coated metal, glass fabric,.. |
|||
| Cure Time | 3.00 min | 0.0500 hour | Tack Free Time |
| Shin-Etsu Silicones KE-347TUV Silicone, RTV Coating Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
| Cure Time | 3.00 min | 0.0500 hour | Tack Free Time |
| Shin-Etsu Silicones KE-3490 Silicone, RTV Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
| Cure Time | 3.00 min | 0.0500 hour | Tack Free Time |
| Shin-Etsu Silicones KE-3490 Silicone, RTV Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
| Cure Time | 3.00 min | 0.0500 hour | |
| Loctite® 3273 Acrylic Bonding Adhesive Acrylic Bonding AdhesivesLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impact, stress and shock resistance. .. |
|||
| Cure Time | 3.00 min | 0.0500 hour | |
| Loctite® 332 Severe Environment Structural Adhesive Acrylic Bonding AdhesivesLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impact, stress and shock resistance. .. |
|||
| Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 350ºF Cure Temperature MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 350ºF Cure Temperature MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 3.00 - 9.00 min | 0.0500 - 0.150 hour | t`50; ASTM D2084 |
| ExxonMobil Exxon™ 2244 Fast Cure Rate Grade Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene. The product form is offwhite to amber bales.Information provided by ExxonMobil Chemical |
|||
| Cure Time | 3.00 min | 0.0500 hour | Curelastmeter |
| Daikin DAI-EL G-901 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Excellent solvent resistance.Information provided by Daikin Industries. |
|||
| Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 76A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 3.00 min @Temperature 177 °C |
0.0500 hour @Temperature 350 °F |
|
| TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
| Cure Time | 3.00 min | 0.0500 hour | Curelastmeter |
| Daikin DAI-EL G-912 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Excellent solvent resistance, good compression set.Information provided by Daikin Industries. |
|||
| Cure Time | 3.00 min | 0.0500 hour | 6 min. @ 130ºC, 3 min. @ 150ºC |
| Loctite® 3889 Rapid Cure Isotropic Epoxy Adhesive Electrically Conductive BondersLoctite® Electrically Conductive Adhesives are used in a variety of applications where electrical connectivity is needed, providing a conductive path where traditiona.. |
|||
| Cure Time | 3.00 - 5.00 min @Temperature 138 - 138 °C |
0.0500 - 0.0833 hour @Temperature 280 - 280 °F |
Average value: 5.17 min Grade Count:1 |
| Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |
|||
| Cure Time | 3.00 - 5.00 min @Thickness 6.35 - 6.35 mm |
0.0500 - 0.0833 hour @Thickness 0.250 - 0.250 in |
Average value: 5.17 min Grade Count:1 |
| Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |
|||