Polymer Property : Cure Time = 2.00 min Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Cure Time	2.00 min	0.0333 hour	On metal (Fixture)
ND Industries 611 Heptane-Acetone Anaerobic Primer General purpose anaerobic primer. On part life 30 days. Non-ozone depleting but flammable solvent
Cure Time	2.00 - 3.00 min	0.0333 - 0.0500 hour	Aluminum, handling time
Permabond 731 Cyanoacrylate, toughened PERMABOND® 731 is a toughened cyanoacrylate with very good impact and peel strength when compared to a conventional cyanoacrylate. It bonds rapidly at room temperature and its viscosity is stable o..
Cure Time	<= 2.00 min	<= 0.0333 hour	handling time, gap ~0mm
Permabond TA435 Toughened Acrylic Adhesive & Initiator PERMABOND TA435 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some thermoplastics. This adhesive may be used in a variety of structural bonding appli..
Cure Time	<= 2.00 min @Temperature 25.0 °C	<= 0.0333 hour @Temperature 77.0 °F	with initiator 44, 50% rh
Permabond TA459 Toughened Acrylic Adhesive Permabond TA459 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some thermoplastics. This product was specifically designed to be non-corrosive to sens..
Cure Time	<= 2.00 min @Temperature 25.0 °C	<= 0.0333 hour @Temperature 77.0 °F	with intiator 44, 50% rh
Permabond TA4590 Toughened Acrylic Adhesive Permabond TA4590 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some thermoplastics. This product was specifically designed to be non-corrosive to sen..
Cure Time	2.00 min	0.0333 hour	Fixture
Resinlab® RC8038 Anaerobic Retaining Compound The RC 8000 Series anaerobic retaining compounds are designed for use in demanding applications to fill the spaces and surface irregularities between tightly mated cylindrical parts. These products ..
Cure Time	2.00 min	0.0333 hour	Fixture
Resinlab® RC8048 Anaerobic Retaining Compound The RC 8000 Series anaerobic retaining compounds are designed for use in demanding applications to fill the spaces and surface irregularities between tightly mated cylindrical parts. These products ..
Cure Time	2.00 min @Temperature 204 °C	0.0333 hour @Temperature 400 °F
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 400ºF Cure Temperature MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Cure Time	2.00 min @Temperature 204 °C	0.0333 hour @Temperature 400 °F
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 400ºF Cure Temperature MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Cure Time	2.00 - 4.00 min	0.0333 - 0.0667 hour
Permabond TA4246 Toughened Acrylic Adhesive PERMABOND® TA4246 is a 2-part, no-mix, room temperature curing structural adhesive. It is ideal for use on a wide variety of substrate materials and forms a very high strength structural bond with ..
Cure Time	2.00 - 3.00 min	0.0333 - 0.0500 hour	Working time
ITW Devcon Plastic Welderâ„¢ Methacrylate Adhesive II, Ultra White Information provided by ITW Devcon
Cure Time	2.00 min	0.0333 hour	Tack Free Time
Shin-Etsu Silicones KE-3479 Silicone, RTV Information Provided by Shin-Etsu Silicones of America, Inc.
Cure Time	2.00 min @Temperature 204 °C	0.0333 hour @Temperature 400 °F
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 400ºF Cure Temperature MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Cure Time	2.00 min @Temperature 204 °C	0.0333 hour @Temperature 400 °F
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 400ºF Cure Temperature MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Cure Time	2.00 min @Temperature 204 °C	0.0333 hour @Temperature 400 °F
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 82A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Cure Time	2.00 min @Temperature 204 °C	0.0333 hour @Temperature 400 °F
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Cure Time	2.00 min	0.0333 hour
Loctite® Assure™ 425 Threadlocker ThreadlockersInvented by Loctite Corporation as a revolutionary method to lock and seal threaded fasteners, Loctite® Liquid Threadlockers have found wide acceptance in a range of applications--from..
Cure Time	2.00 min	0.0333 hour
Loctite® PRISM® 4210 Instant Adhesive Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-..
Cure Time	2.00 min	0.0333 hour	ts2, Target; ASTM D2084 (mod)
ExxonMobil Chlorobutyl 1066 Rubber Product Description: Exxon™ Chlorobutyl rubber is a copolymer of isobutylene and isoprene. The product has characteristic specific gravity of 0.93. The product form is white to light amber bales.In..
Cure Time	2.00 - 8.00 min	0.0333 - 0.133 hour	t'50; ASTM D2084 (mod)
ExxonMobil Chlorobutyl 1066 Rubber Product Description: Exxon™ Chlorobutyl rubber is a copolymer of isobutylene and isoprene. The product has characteristic specific gravity of 0.93. The product form is white to light amber bales.In..
Cure Time	2.00 - 8.00 min	0.0333 - 0.133 hour	t`50; ASTM D2084
ExxonMobil Exxon™ 1068 Exxon Chloromobutyl is a chlorinated copolymer of isobutylene and isoprene.Information provided by ExxonMobil Chemical
Cure Time	2.00 min	0.0333 hour	Curelastmeter
Daikin DAI-EL G-952 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 69% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Good solvent resistance and low-temperature characteristics.Information provided by Daikin Industrie..
Cure Time	2.00 min	0.0333 hour	Set Time
3M Scotch-Weld™ EZ250120 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds well to wood and wood bases surfaces as w..
Cure Time	2.00 min	0.0333 hour	Set Time
3M Scotch-Weld™ TE200 Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as ..
Cure Time	2.00 min	0.0333 hour	Full
3M FIP 1-Step Fire Barrier Rated Foam 3M Fire Barrier Rated Foam (FIP 1-Step), is a smoke, sound, and firestopping foam for wall and floor penetrations. Premium two-part, easy-to-handle formulations. Expands up to five times during inst..
Cure Time	2.00 min	0.0333 hour	Tack-Free, 10 g, 1/4" thick @ RT
3M Scotch-Weld™ DP600NS Concrete Repair and Self-Leveling 3M™ Scotch-Weld™ Concrete Repair Self-Leveling DP600NS is a gray, rapid setting, two component polyurethane. It is packaged as a 1:1 ratio liquid in a duo-pack cartridge. With the squeeze of a tri..
Cure Time	2.00 min	0.0333 hour	Time to Handling Strength
3M Scotch-Weld™ DP601NS Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are gray, rapid, setting, two component polyurethanes. They are packaged as 1:1 ratio liquids in a duo-pack cartridge. With the squeeze of a trigger, the compon..
Cure Time	2.00 min @Temperature 204 °C	0.0333 hour @Temperature 400 °F
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 82A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Cure Time	2.00 min @Temperature 204 °C	0.0333 hour @Temperature 400 °F
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Cure Time	2.00 - 8.00 min	0.0333 - 0.133 hour	t`50; ASTM D2084
ExxonMobil Exxon™ 1066 Exxon Chloromobutyl is a chlorinated copolymer of isobutylene and isoprene.Information provided by ExxonMobil Chemical