Processing Properties	Metric	English	Comments
Cure Time	13.0 min @Temperature 68.3 °C	0.217 hour @Temperature 155 °F	Press cured
TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR Talc-Mistron Vapor MILLATHANE E34 is a high performance polyether polyurethane rubber for applications requiring: high abrasion resistance, low temperature flexibility, ozone resistance, oil and fuel resistance, outst..
Cure Time	13.0 min @Temperature 160 °C	0.217 hour @Temperature 320 °F	Press cured
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.0 PHR Zinc Stearate MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st..
Cure Time	13.0 min @Temperature 166 °C	0.217 hour @Temperature 330 °F
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 330ºF Cure Temperature MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st..
Cure Time	13.0 min @Temperature 68.3 °C	0.217 hour @Temperature 155 °F	Press cured
TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR Talc-Mistron Vapor MILLATHANE E34 is a high performance polyether polyurethane rubber for applications requiring: high abrasion resistance, low temperature flexibility, ozone resistance, oil and fuel resistance, outst..
Cure Time	13.0 min @Temperature 160 °C	0.217 hour @Temperature 320 °F	Press cured
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.0 PHR Zinc Stearate MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st..
Cure Time	13.0 min @Temperature 160 °C	0.217 hour @Temperature 320 °F	Press cured
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR Thanecure® ZM MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st..
Cure Time	13.0 min @Temperature 155 °C	0.217 hour @Temperature 311 °F
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 50A, Black Sulfur Cure Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m..
Cure Time	13.0 min @Temperature 160 °C	0.217 hour @Temperature 320 °F	Press cured
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR Thanecure® ZM MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st..
Cure Time	13.0 min @Temperature 166 °C	0.217 hour @Temperature 330 °F
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 330ºF Cure Temperature MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st..
Cure Time	13.0 min @Temperature 155 °C	0.217 hour @Temperature 311 °F
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 50A, Black Sulfur Cure Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m..