Polymer Property : Cure Time = 0.0250 hour Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Processing Properties Metric English Comments
Cure Time 1.50 - 1440 min
0.0250 - 24.0 hour
Average value: 372 min Grade Count:32
Overview of materials for Methacrylate Adhesive
This property data is a summary of similar materials in the MatWeb database for the category "Methacrylate Adhesive". Each property range of values reported is minimum and maximum values of appropri..
Cure Time 1.50 min
0.0250 hour
Handling
Palm Labs Adhesives TURBO-LOCK SERIES 20 Anaerobic Thread Locking Compound
TURBO-LOCK SERIES 20 is a fast curing, BLUE, low strength, thread locker for bonding and sealing small plastic fasteners. It is highly resistance to heat, vibrations, water, gases, oils, hydrocarbon..
Cure Time 1.50 - 2.83 min
0.0250 - 0.0472 hour
Gelation time
Mitsui MILEXâ„¢ XL-325M Phenol Aralkyl Resin, High Molecular Weight
The MILEXâ„¢ Family of products is widely featured in brake systems of automobiles made by automakers through Mitsui Chemicals'. The phenolic material is primarily used as binders in brake pad..
Cure Time 1.50 min
0.0250 hour
Loctite® 334 Acrylic Bonding Adhesive
Acrylic Bonding AdhesivesLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impact, stress and shock resistance. ..
Cure Time 1.50 min
0.0250 hour
Loctite® 410 Toughened Ethyl Cyanoacrylate Bonding Adhesive
Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-..
Cure Time 1.50 min
0.0250 hour
Loctite® 455 Low odor/low bloom Alkoxy Cyanoacrylate Bonding Adhesive
Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-..
Cure Time 1.50 - 6.50 min
0.0250 - 0.108 hour
ts2; ASTM D2084
ExxonMobil Exxon™ 2211 Fast Cure Rate Grade
Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene. The product form is offwhite to amber balesInformation provided by ExxonMobil Chemical
Cure Time 1.50 - 6.50 min
0.0250 - 0.108 hour
ts2; ASTM D2084
ExxonMobil Exxon™ 2222 Regular Cure Rate Grade
Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene. The product for is white to light amber bales.Information provided by ExxonMobil Chemical
Cure Time 1.50 - 6.50 min
0.0250 - 0.108 hour
ts2; ASTM D2084
ExxonMobil Exxon™ 2235 Regular Cure Rate Grade
Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene. The product form is white to light amber bales.Information provided by ExxonMobil Chemical
Cure Time 1.50 - 6.50 min
0.0250 - 0.108 hour
ts2; ASTM D2084
ExxonMobil Exxon™ 2255 Regular Cure Rate Grade
Exxon Bromobutyl is a brominated copolymer of isobutylene and isoprene.The product form is white to light amber bales.Information provided by ExxonMobil Chemical
Cure Time 1.50 min
0.0250 hour
Curelastmeter
Daikin DAI-EL LT-302 Fluoroelastomer, Low Temperature Grade, 64% Fluorine Content
Features: Flexible up to -30°C, excellent low temperature sealing.Information provided by Daikin Industries.
Cure Time 1.50 min

@Pressure 0.345 MPa,
Temperature 121 °C
0.0250 hour

@Pressure 50.0 psi,
Temperature 250 °F
Recommended Cure Cycle
Arlon 51981XA015 0.0150" Uncured Silicone Rubber with Fiberglass Substrate
Design/Construction:Interleave 1: 2.5 mil PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Style 7628 FiberglassSide 2: Uncured Silicone RubberInterleave 2: 2.5 mil PolyethyleneThis data r..
Cure Time 1.50 - 1.83 min
0.0250 - 0.0306 hour
per mm
Amity Thermosets ATS 1613-R Phenolic Molding Nylon and glass Filler, Compression Molded
Characteristics:High dielectric & mechanical strengthWeather resistant Good electric insulationLow water absorption Good mechanical tension bearing capacityColor-blackMedium flow Applications:Railwa..
Cure Time 1.50 - 2.00 min

@Temperature 204 - 232 °C
0.0250 - 0.0333 hour

@Temperature 400 - 450 °F
Unifrax Fiberfrax® Duraset® Flet
Fiberfrax® Lo-Con™ felt and Duraset® flet are unique product forms in the Unifrax Corporation's extensive ceramic fiber product family. Felt products extend the performance of Fiberfrax papers i..
Cure Time 1.50 min
0.0250 hour
Loctite® Black Max® 380 Instant Adhesive
Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-..
Cure Time 1.50 min

@Temperature 150 °C
0.0250 hour

@Temperature 302 °F
Loctite® CHIPBONDER® 348 General Purpose, Syringe Dispense
Surface Mount AdhesivesLoctite® Chipbonder® Surface Mount Adhesives (SMAs) maintain component positioning during wave solder and solder reflow processes. Loctite offers a variety of application te..
Cure Time 1.50 min

@Temperature 150 °C
0.0250 hour

@Temperature 302 °F
Loctite® CHIPBONDER® 3609 Syringe Dispense
Surface Mount AdhesivesLoctite® Chipbonder® Surface Mount Adhesives (SMAs) maintain component positioning during wave solder and solder reflow processes. Loctite offers a variety of application te..
Cure Time 1.50 min

@Temperature 150 °C
0.0250 hour

@Temperature 302 °F
Loctite® CHIPBONDER® 3610 Syringe Dispense
Surface Mount AdhesivesLoctite® Chipbonder® Surface Mount Adhesives (SMAs) maintain component positioning during wave solder and solder reflow processes. Loctite offers a variety of application te..
Cure Time 1.50 min

@Temperature 100 °C
0.0250 hour

@Temperature 212 °F
Loctite® CHIPBONDER® 3619 Low Temperature Cure, Syringe Dispense
Surface Mount AdhesivesLoctite® Chipbonder® Surface Mount Adhesives (SMAs) maintain component positioning during wave solder and solder reflow processes. Loctite offers a variety of application te..
Cure Time 1.50 min

@Pressure 0.345 MPa,
Temperature 121 °C
0.0250 hour

@Pressure 50.0 psi,
Temperature 250 °F
Recommended Cure Cycle
Arlon 48981R010 0.0100" Uncured Silicone Rubber with Fiberglass Substrate
Design/Construction:Interleave 1: 3 mil PolyethyleneSide 1: Uncured RubberSubstrate: Style 1080 FiberglassSide 2: Uncured Silicone RubberInterleave 2: 3 mil PolyethyleneThis data represents typic..
Cure Time 1.50 min
0.0250 hour
Loctite® 480 Toughened Ethyl Cyanoacrylate Bonding Adhesive
Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-..
Cure Time 1.50 min

@Temperature 150 °C
0.0250 hour

@Temperature 302 °F
Loctite® CHIPBONDER® 3621 Ultra High Speed, Syringe Dispense
Surface Mount AdhesivesLoctite® Chipbonder® Surface Mount Adhesives (SMAs) maintain component positioning during wave solder and solder reflow processes. Loctite offers a variety of application te..
Cure Time 1.50 - 4320 min
0.0250 - 72.0 hour
Average value: 324 min Grade Count:27
Overview of materials for Thermoset Fluoroelastomer
This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Fluoroelastomer". Each property range of values reported is minimum and maximum values of appr..