Polymer Property : Cure Time = 16.0 hour Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 960 - 1440 min @Temperature 25.0 °C |
16.0 - 24.0 hour @Temperature 77.0 °F |
|
| Resinlab® EP1285HD-9 Highly Filled, Medium Viscosity Casting Resin Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low C.. |
|||
| Cure Time | 960 min @Temperature 82.2 °C |
16.0 hour @Temperature 180 °F |
Complete Cure Cycle |
| Northstar Polymers MGB-A90A High Performance Polyurethane Cast Elastomer System 90A This is a PTMEG/MDI base high-performance polyurethane casting system. This system is recommended to applications in which the part requires high rebound, slide abrasion, constant water contact and.. |
|||
| Cure Time | 960 - 1440 min @Temperature 82.2 °C |
16.0 - 24.0 hour @Temperature 180 °F |
Complete Cure Cycle |
| Northstar Polymers MSS-A80AQ High Performance Polyurethane Cast Elastomer System 80A This is a Ester/MDI base high-performance polyurethane casting system. This systems is recommended to applications in which the part requires high tensile strength, cut/tear resistance, dry-abrasio.. |
|||
| Cure Time | 960 min @Temperature 82.2 °C |
16.0 hour @Temperature 180 °F |
Complete Cure Cycle |
| Northstar Polymers MSS-A90A High Performance Polyurethane Cast Elastomer System 90A This is a Ester/MDI base high-performance polyurethane casting system. This systems is recommended to applications in which the part requires high tensile strength, cut/tear resistance, dry-abrasio.. |
|||
| Cure Time | 960 min @Temperature 82.2 °C |
16.0 hour @Temperature 180 °F |
Complete Cure Cycle |
| Northstar Polymers MGG-A70DQ High Performance Polyurethane Cast Elastomer System 70A This is a PTMEG/MDI base high-performance polyurethane casting system. This system is recommended to applications in which the part requires high rebound, slide abrasion, constant water contact and.. |
|||
| Cure Time | 960 - 1440 min @Temperature 25.0 °C |
16.0 - 24.0 hour @Temperature 77.0 °F |
|
| Trelleborg Emerson & Cuming Eccobond® 15 LV Clear Variable Hardness Low Viscosity Catalyst Emerson & Cuming 15 LV Clear Eccobond® Variable Hardness Low Viscosity CatalystLow viscosity. Easy-to-use, simple mix ratios. Hardness of cured castings can be controlled by the amount of hardener .. |
|||
| Cure Time | 960 - 1440 min @Temperature 25.0 °C |
16.0 - 24.0 hour @Temperature 77.0 °F |
|
| Trelleborg Emerson & Cuming Eccobond® 15 LV Variable Hardness Low Viscosity Catalyst Emerson & Cuming 15 LV Eccobond® Variable Hardness Low Viscosity CatalystLow viscosity. Easy-to-use, simple mix ratios. Hardness of cured castings can be controlled by the amount of hardener used. .. |
|||
| Cure Time | 960 - 1440 min @Temperature 25.0 °C |
16.0 - 24.0 hour @Temperature 77.0 °F |
|
| Trelleborg Emerson & Cuming Eccobond® 23 LV General Purpose Catalyst Emerson & Cuming 23 LV Eccobond® General Purpose CatalystExcellent low temperature performance properties, excellent thermal shock/cycle and impact resistance. Good hardener for cryogenic applicati.. |
|||
| Cure Time | 960 - 1440 min @Temperature 25.0 °C |
16.0 - 24.0 hour @Temperature 77.0 °F |
|
| Trelleborg Emerson & Cuming Eccobond® 43 Heat Cure Catalyst Emerson & Cuming 43 Eccobond® Heat Cure CatalystRoom temperature gelling version of 28. Excellent for low stress potting and bonding. Will post cure in actual use. Combines the benefits of both 9 a.. |
|||
| Cure Time | 960 min @Temperature 23.0 °C |
16.0 hour @Temperature 73.4 °F |
|
| Loctite® 3171 Deep Potting Polyurethane PottersLoctite® Potting materials are used on electronic device housings to enhance mechanical strength, provide electrical insulation and enhance vibration and shock resistance of assemblies.For e.. |
|||
| Cure Time | 960 min @Temperature 32.0 °C |
16.0 hour @Temperature 89.6 °F |
Full Load |
| Chesterton ARC 10 Paste grade machinable composite Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance and corrosion resistance. It is non-sag.. |
|||
| Cure Time | 960 min @Temperature 10.0 °C |
16.0 hour @Temperature 50.0 °F |
Foot Traffic |
| Chesterton ARC 791 Composite Description: A quartz reinforced composite designed to resurface and restore concrete surfaces, to protect new concrete, and to repair concrete damaged by chemical and physical abuse. ARC 791 has ex.. |
|||
| Cure Time | 960 min @Temperature 32.0 °C |
16.0 hour @Temperature 89.6 °F |
Full Load |
| Chesterton ARC 858 Abrasion resistant rebuilding and faring composite An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 0.15 mm (60 mils) or m.. |
|||
| Cure Time | 960 min @Temperature 16.0 °C |
16.0 hour @Temperature 60.8 °F |
Tack Free |
| Chesterton ARC 982 100% Novolac acid resistant coating Description: An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. A low viscosity composite that is applied by brush, squeegee, or a plural compo.. |
|||
| Cure Time | 960 min @Temperature 10.0 °C |
16.0 hour @Temperature 50.0 °F |
Foot Traffic |
| Chesterton ARC CS4 low-viscosity, 100% solids, barrier coating Description: An advanced composite formulated to protect concrete surfaces from harsh chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat in a 2 coat syst.. |
|||
| Cure Time | 960 min @Temperature 25.0 °C |
16.0 hour @Temperature 77.0 °F |
Light Load |
| Chesterton ARC CS4 low-viscosity, 100% solids, barrier coating Description: An advanced composite formulated to protect concrete surfaces from harsh chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat in a 2 coat syst.. |
|||
| Cure Time | 960 min @Temperature 32.0 °C |
16.0 hour @Temperature 89.6 °F |
Full Load |
| Chesterton ARC MX1 Vertical Build Extreme Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It is applied at a thickness of 6 mm (1/4”).. |
|||
| Cure Time | 960 min @Temperature 29.0 °C |
16.0 hour @Temperature 84.2 °F |
Full Chemical |
| Chesterton ARC S7 High Temperature & Chemical Resistant Novolac Vinyl Ester Coating Description: ARC S7 is a low VOC, epoxy novolac vinyl ester based coating intended for high temperature exposures in chemically aggressive applications where the risk for thermal cycling may be pres.. |
|||
| Cure Time | 960 min @Temperature 60.0 °C |
16.0 hour @Temperature 140 °F |
|
| Cytec (Conap) FR-1050 Conapoxy® Resin / Conacure® Hardener Epoxy Potting and Encapsulating Systems for Electronic ApplicationsHigh technology epoxy resin systems for potting and encapsulation, for the defense, aerospace, electronics, computer, automotive an.. |
|||
| Cure Time | 960 min @Temperature 80.0 °C |
16.0 hour @Temperature 176 °F |
|
| Cytec EN-13 (Conap) Casting, Potting, and Molding Compound High Technology Potting, Casting and Molding CompoundsTwo-component, polybutadiene-based liquid urethane casting and potting systems. When reacted these high technology systems produce tough, stable.. |
|||
| Cure Time | 960 min @Temperature 80.0 °C |
16.0 hour @Temperature 176 °F |
|
| Cytec EN-14 (Conap) Casting, Potting, and Molding Compound High Technology Potting, Casting and Molding CompoundsTwo-component, polybutadiene-based liquid urethane casting and potting systems. When reacted these high technology systems produce tough, stable.. |
|||
| Cure Time | 960 min @Temperature 80.0 °C |
16.0 hour @Temperature 176 °F |
|
| Cytec EN-2532 (Conap) Potting and Encapsulation Adhesive Polyurethane Potting and Encapsulating SystemsConathane® EN-2500 series polyurethane potting and encapsulating systems from Cytek have varying degrees of worklife, viscosity and hardness for many s.. |
|||
| Cure Time | 960 min @Temperature 80.0 °C |
16.0 hour @Temperature 176 °F |
|
| Cytec EN-8 (Conap) Casting, Potting, and Molding Compound High Technology Potting, Casting and Molding CompoundsTwo-component, polybutadiene-based liquid urethane casting and potting systems. When reacted these high technology systems produce tough, stable.. |
|||
| Cure Time | 960 min @Temperature 150 °C |
16.0 hour @Temperature 302 °F |
|
| Dow Corning JCR 6109 One-part, translucent, low modulus LED gel encapsulant with a very long working time.Information provided by Dow Corning |
|||
| Cure Time | 960 min @Temperature 10.0 °C |
16.0 hour @Temperature 50.0 °F |
Tack Free |
| Chesterton ARC MX2 High Wear Fine Particle Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”.. |
|||
| Cure Time | 960 min @Temperature 95.0 °C |
16.0 hour @Temperature 203 °F |
|
| Abatron AboCast/AboCure 8502-1 Epoxy AboCast/AboCure 8502-1 is a solventless clear Epoxy System, used as a casting, adhesive, and impregnating resin for transformers, capacitors, coils, and other electronic components requiring a low-v.. |
|||
| Cure Time | 960 - 1440 min @Temperature 24.0 °C |
16.0 - 24.0 hour @Temperature 75.2 °F |
demold time |
| BCC Products BC 8990 Polyurethane Elastomer BC8990 is a two-component urethane elastomer compound specifically designed for general purpose molding and casting of various shapes. This product is a safe, easy-to-handle, room temperature mixing.. |
|||
| Cure Time | 960 min @Temperature 26.0 °C |
16.0 hour @Temperature 78.8 °F |
Full Chemical |
| Chesterton ARC NVE VC Vinyl Ester Sealer Description: ARC NVE VC (Veil Coat) is a two-component, modified epoxy novolac vinyl ester sealer coat formulated for application by brush, roller or spray at 0.15-0.25 mm (0.07-0.010”) wet film th.. |
|||
| Cure Time | 960 min @Temperature 32.0 °C |
16.0 hour @Temperature 89.6 °F |
Full Load |
| Chesterton MRS 10 Metal Rebuilding System Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance It is non-sagging, non-shrinking and 10.. |
|||
| Cure Time | 960 min @Temperature 43.0 °C |
16.0 hour @Temperature 109 °F |
Overcoat End |
| Chesterton ARC S1HB Sprayable high-viscosity, 100% solids, advanced coating An advanced composite formulated to protect concrete and metal surfaces from corrosion and chemical attack. It is normally applied at a thickness of 1-2 mm (40-80 mils) per coat. However, greater si.. |
|||