Polymer Property : Specific Heat Capacity = 0.586 J/g-°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, weld metal as welded
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 600.0 °C
 0.140 BTU/lb-°F

@Temperature 1112 °F
 hardened and tempered
Bohler-Uddeholm UDDEHOLM VANADIS 30 AISI M2 + Co SUPERCLEAN 3 Powder Metallurgical Cold Work Tool Steel
Uddeholm Vanadis 30 is a Co high alloyed powder metallurgy high speed steel corresponding to AISI M3:2 + Co. The high compressive strength, 67 HRC, and good abrasive wear resistance makes Uddeholm V..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 600.0 °C
 0.140 BTU/lb-°F

@Temperature 1112 °F
 hardened and tempered
Bohler-Uddeholm UDDEHOLM VANADIS 60 Powder Metallurgically Produced Tool Steel
Uddeholm Vanadis 60 is a high alloyed powder metallurgical high speed steel suitable for very demanding cold work applications and for cutting tools. The high carbon and alloying content, Co, Mo, W ..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 600 °C
 0.140 BTU/lb-°F

@Temperature 1110 °F
 hardened and tempered condition
Assab Steels ASP 60 Cold Work Steel
ASP 60 is a W-Mo-V-Co alloyed PM high speed steel characterized by:Highest wear resistanceMaximum compressive strengthGood through hardening propertiesGood toughnessGood dimensional stability on hea..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 600 °C
 0.140 BTU/lb-°F

@Temperature 1110 °F
 hardened and tempered condition
Assab Steels ASP 30 Cold Work Steel
ASP 30 is a W-Mo-v-Co alloyed PM high speed steel characterized by:High wear resistanceHigh compressive strength at high hardnessGood through hardening propertiesGood toughnessGood dimensional stabi..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Specific Heat Capacity 0.586 J/g-°C

@Temperature 620 °C
 0.140 BTU/lb-°F

@Temperature 1150 °F
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..