- Polymer Property : Specific Heat Capacity = 0.456 J/g-°C
Polymer Property : Specific Heat Capacity = 0.456 J/g-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 300 °C |
0.109 BTU/lb-°F @Temperature 572 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 300 °C |
0.109 BTU/lb-°F @Temperature 572 °F |
|
| Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 23.0 °C |
0.109 BTU/lb-°F @Temperature 73.4 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 23.0 °C |
0.109 BTU/lb-°F @Temperature 73.4 °F |
|
| Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 23.0 °C |
0.109 BTU/lb-°F @Temperature 73.4 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 23.0 °C |
0.109 BTU/lb-°F @Temperature 73.4 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 23.0 °C |
0.109 BTU/lb-°F @Temperature 73.4 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 23.0 °C |
0.109 BTU/lb-°F @Temperature 73.4 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 23.0 °C |
0.109 BTU/lb-°F @Temperature 73.4 °F |
|
| Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 23.0 °C |
0.109 BTU/lb-°F @Temperature 73.4 °F |
|
| Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 600 °C |
0.109 BTU/lb-°F @Temperature 1110 °F |
|
| HP Alloys Alloy B-2, Solution Treated, 40% Cold Worked Solution Treated, 40% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 300 °C |
0.109 BTU/lb-°F @Temperature 572 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 250 °C |
0.109 BTU/lb-°F @Temperature 482 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 600 °C |
0.109 BTU/lb-°F @Temperature 1110 °F |
|
| HP Alloys Alloy B-2, Solution Treated, 50% Cold Worked Solution Treated, 50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 300 °C |
0.109 BTU/lb-°F @Temperature 572 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 300 °C |
0.109 BTU/lb-°F @Temperature 572 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||