Polymer Property : Specific Heat Capacity = 0.142 BTU/lb-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Specific Heat Capacity 0.594 J/g-°C

@Temperature 850 °C
0.142 BTU/lb-°F

@Temperature 1560 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 750 °C
0.142 BTU/lb-°F

@Temperature 1380 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 850 °C
0.142 BTU/lb-°F

@Temperature 1560 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 850 °C
0.142 BTU/lb-°F

@Temperature 1560 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 850 °C
0.142 BTU/lb-°F

@Temperature 1560 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 850 °C
0.142 BTU/lb-°F

@Temperature 1560 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 750 °C
0.142 BTU/lb-°F

@Temperature 1380 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 700 °C
0.142 BTU/lb-°F

@Temperature 1290 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 700 °C
0.142 BTU/lb-°F

@Temperature 1290 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 700 °C
0.142 BTU/lb-°F

@Temperature 1290 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 750 °C
0.142 BTU/lb-°F

@Temperature 1380 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 750 °C
0.142 BTU/lb-°F

@Temperature 1380 °F
Haynes Hastelloy® S alloy, weld metal, aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, weld metal, aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 750 °C
0.142 BTU/lb-°F

@Temperature 1380 °F
Haynes Hastelloy® S alloy, weld metal, aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 850 °C
0.142 BTU/lb-°F

@Temperature 1560 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 900 °C
0.142 BTU/lb-°F

@Temperature 1650 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 750 °C
0.142 BTU/lb-°F

@Temperature 1380 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 700 °C
0.142 BTU/lb-°F

@Temperature 1290 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 750 °C
0.142 BTU/lb-°F

@Temperature 1380 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 850 °C
0.142 BTU/lb-°F

@Temperature 1560 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Specific Heat Capacity 0.594 J/g-°C

@Temperature 750 °C
0.142 BTU/lb-°F

@Temperature 1380 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..