| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, 20% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, 40% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, 50% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, 60% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW weld, C-22 base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GMAW spray weldment, 23.4 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GTAW weldment, sheet - plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 50.0 °C |
0.0989 BTU/lb-°F @Temperature 122 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, 60% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Specific Heat Capacity | 0.414 J/g-°C @Temperature 52.0 °C |
0.0989 BTU/lb-°F @Temperature 126 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||