Polymer Property : CTE, linear, Transverse to Flow = 40.7 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Transverse to Flow | 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| SABIC Innovative Plastics Valox® 4022 PBT (Europe-Africa-Middle East) VALOX 4022 is a 20% high strength glass fibre reinforced PBT injection moulding resin, with improved mechanical properties. Applications : Spotlights, appliance housings and handles. |
|||
| CTE, linear, Transverse to Flow | 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific) LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System. |
|||
| CTE, linear, Transverse to Flow | 73.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific) LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System. |
|||
| CTE, linear, Transverse to Flow | 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66 LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| CTE, linear, Transverse to Flow | 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66 LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| CTE, linear, Transverse to Flow | 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66 LNP THERMOCOMP* RF006XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber |
|||
| CTE, linear, Transverse to Flow | 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66 LNP THERMOCOMP* RF006XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber |
|||
| CTE, linear, Transverse to Flow | 73.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP LUBRICOMP DL002P PC LNP LUBRICOMP* DL002P is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Exceptional Processing, Internally Lubricated. |
|||
| CTE, linear, Transverse to Flow | 73.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System. |
|||
| CTE, linear, Transverse to Flow | 73.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System. |
|||