Polymer Property : Thermal Conductivity = 188 BTU-in/hr-ftÂ²-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 538Â°C (1000Â°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 538Â°C (1000Â°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 538Â°C (1000Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 760Â°C (1400Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 760Â°C (1400Â°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 760Â°C (1400Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, gas tungsten arc welded, aged at 538Â°C (1000Â°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427Â°C (800Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427Â°C (800Â°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427Â°C (800Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871Â°C (1600Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871Â°C (1600Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, weld metal, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 950 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1740 Â°F
Haynes HastelloyÂ® S alloy, weld metal, aged at 649Â°C (1200Â°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Thermal Conductivity	27.1 W/m-K @Temperature 200 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 392 Â°F
Latrobe LSSâ„¢ Chipper Knife Tool Steel (ASTM A8 Mod.) TLS Chipper Knife tool steel is an air-hardening, 8% chromium tool steel which exhibits very good wear resistance and toughness. TLS Chipper Knife exhibits wear resistance which is better than that..
Thermal Conductivity	27.1 W/m-K @Temperature 649 Â°C	188 BTU-in/hr-ftÂ²-Â°F @Temperature 1200 Â°F
Latrobe Magnadieâ„¢ Modified H-13 Hot Work Die Steel MAGNADIE is an AOD refined, air hardenable 5% chromium die steel. It is a good choice for both hot and cold work applications. Magnadie steel possesses improved toughness as compared to standard H-..
Thermal Conductivity	27.1 W/m-K @Temperature 950 °C	188 BTU-in/hr-ft²-°F @Temperature 1740 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Thermal Conductivity	27.1 W/m-K @Temperature 950 °C	188 BTU-in/hr-ft²-°F @Temperature 1740 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Thermal Conductivity	27.1 W/m-K @Temperature 950 °C	188 BTU-in/hr-ft²-°F @Temperature 1740 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Thermal Conductivity	27.1 W/m-K @Temperature 649 °C	188 BTU-in/hr-ft²-°F @Temperature 1200 °F
Latrobe Magnadie - RF Modified Premium H-13 Hot Work Die Steel Magnadie-RF is a premium quality 5% chromium hot work die steel. The chemistry of Magnadie-RF steel is a modification of the premium quality H-13 chemistry. Magnadie-RF steel is designed for incre..
Thermal Conductivity	27.1 W/m-K @Temperature 950 °C	188 BTU-in/hr-ft²-°F @Temperature 1740 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..