- Polymer Property : Thermal Conductivity = 112 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 112 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 400 °C |
112 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 400 °C |
112 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 400 °C |
112 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 400 °C |
112 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 400 °C |
112 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 20.0 °C |
112 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| EDRO UltraChem® ESR #16 Precipitation Hardening Stainless Mold Steel Ultrachem ESR® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by exceptional polishability, exceptional corrosion resistance, unifor.. |
|||
| Thermal Conductivity | 16.2 W/m-K @Temperature 100 °C |
112 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| AK Steel 304 Austenitic Stainless steel AK Steel 304 is a variation of the basic 18-8 grade, Type 302. Lower carbon, in Type 304, minimizes chromium carbide precipitation due to welding and its susceptibility to intergranular corrosion. .. |
|||
| Thermal Conductivity | 16.2 W/m-K @Temperature 100 °C |
112 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| AK Steel 316 Austenitic Stainless steel AK Steel 316 contains molybdenum. This addition increases general corrosion resistance, improves resistance to pitting from chloride ion solutions, and provides increased strength at elevated tempe.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 200 °C |
112 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |
|||
| Thermal Conductivity | 16.1 W/m-K @Temperature 300 °C |
112 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||