Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness Tensile strength (ultimate and yield), shear strength, and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness samples. Density a.. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, Solution Treated Tensile strength (ultimate and yield), and elongation values reported here are typical for Cold Rolled Sheet, Solution Treated samples. Density and magnetic permeability are typical of annealed INCO.. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, Solution Treated Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, Solution Treated samples. Density and magnetic permeability are typical of .. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter Tensile strength (ultimate and yield), compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diamete.. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 65% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 85% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 85% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 30% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 40% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 40% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 65% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
Elgiloy® Co-Cr-Ni Alloy, Wire The strength and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fatigue life, and.. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |