Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 9.40 - 10.8 W/m-K | 65.2 - 75.0 BTU-in/hr-ft²-°F | |
Pyrotek Pyrocast SC-2600 Castable Refractory Pyrocast SC-2600 is a high purity silicon carbide based refractory for applications requiring high thermal conductivity, resistance to metal and flame abrasion.ApplicationsFilter boxes Burner tubes .. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | |
ATI Allegheny Ludlum AL 22™ Nickel-Base Alloy, UNS N06022 AL 22 alloy is a Ni-Cr-Mo alloy that provides outstanding resistance to pitting, crevice corrosion, intergranular attack, and stress corrosion cracking. The combination of Cr, Ni, Mo, and W provide.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 20% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | |
Kennametal Stellite Stellite® 25 Cobalt Chromium Cast Alloy Stellite alloy 25 forms a protective oxide film during hot metal-on metal wear which prevents metal transfer and damage due to adhesion. The alloy is resistant to thermal cracking and surface fatig.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 9.40 W/m-K | 65.2 BTU-in/hr-ft²-°F | RT |
Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |