Polymer Property : Thermal Conductivity = 23.6 W/m-K Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, weld metal as welded
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Thermal Conductivity 23.6 W/m-K

@Temperature 700 °C
164 BTU-in/hr-ft²-°F

@Temperature 1290 °F
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..