Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 20% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 10% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 30% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |