- Polymer Property : Thermal Conductivity = 144 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 144 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K | 144 BTU-in/hr-ft²-°F | |
| SGL Carbon Group EK 3205 Carbon Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 593 °C |
144 BTU-in/hr-ft²-°F @Temperature 1100 °F |
|
| ATI Allegheny Ludlum Altemp® HX Nickel-Based superalloy Characteristics: outstanding resistance to oxidation at high temperatures, exceptional strength at elevated temperatures, good fabricability, good machinability in annealed condition, work hardening.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.7 W/m-K @Temperature 600 °C |
144 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||