Polymer Property : Thermal Conductivity = 12.8 W/m-K Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy sheet
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 10% cold reduction
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 20% cold reduction
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 40% cold reduction
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 50% cold reduction
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 50% cold reduction, 925°C for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, sheet, 100 hours exposure at 870°C (1600°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 10% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 30% cold reduction
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity 12.8 W/m-K

@Temperature 100 °C
88.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..