Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 92.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
51.1 µin/in-°F @Temperature 73.4 - 140 °F |
|
Murtfeldt Murytal® C Blue [FS] Acetal Copolymer Thanks to their extremely low absorption of moisture, Murytal® materials are ideally suited for use as electronic isolation components. A fine crystalline structure and high yield strength mean th.. |
|||
CTE, linear | 92.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
51.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-2:1999 |
Nylacast POM C Acetal Copolymer The copolymer grade is the ideal combination of strength, stiffness and wears resistance. It absorbs very little moisture, is easily machinable and is genuinely porosity-free making it the preferred.. |
|||
CTE, linear | 92.0 µm/m-°C @Temperature 20.0 °C |
51.1 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Ineos ABS Lustran® 1148 General Purpose, High-Impact
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionLANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with La.. |
|||
CTE, linear | 92.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
51.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-2:1999 |
Global EPP POM C Acetal Copolymer Polyacetals are highly crystalline thermoplastics, characterised by their high mechanical strength, rigidity and impact resistance. Acetal absorbs very little moisture, enabling the product to maint.. |
|||
CTE, linear | 92.0 µm/m-°C @Temperature -30.0 - 100 °C |
51.1 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
LyondellBasell Hifaxâ„¢ DR279 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ DR279 high melt flow, 1,200 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has a unique balance of stiffness, impact resistance, processability.. |