Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
|
Omnia Plastica Akulon® PA 66 - Akulon 66 - Dry Polyamide obtained by the polymerisation of Hexamethylenediamine and Adipic acid. It is one of the oldest engineering plastics, having been created in the USA in 1930. Due to its origin it is widely.. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
dry sample |
Omnia Plastica Akulon® PA 66.6 - Akulon GX - at 50% RH Copolymer of nylon with excellent mechanical features, it combines the good impact resistances of PA6 as well as the higher stiffness of PA66. For this reason it machines very well on automatic tool.. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
|
Omnia Plastica Akulon® PA 66.6 Akulon GX - Dry Copolymer of nylon with excellent mechanical features, it combines the good impact resistances of PA6 as well as the higher stiffness of PA66. For this reason it machines very well on automatic tool.. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 100 °C |
47.2 µin/in-°F @Temperature 73.4 - 212 °F |
|
Quadrant EPP Ertalyte® TX PET + solid lubricant, extruded (ISO Data) Ertalyte TX is a polyethylene terephthalate compound incorporating a uniformly dispersed solid lubricant. Its specific formulation makes it a premium internally lubricated bearing-grade. Ertalyte TX.. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 100 °C |
47.2 µin/in-°F @Temperature 73.4 - 212 °F |
|
Quadrant EPP Fluorosint® 207 PTFE + mica, compression moulded (ISO Data) This material has a food contact compliant composition which, in combination with the good mechanical performance, dimensional stability, sliding and wear properties and inherent outstanding chemica.. |
|||
CTE, linear | 85.0 µm/m-°C | 47.2 µin/in-°F | |
Permabond UV7141 UV-curable Adhesive Permabond UV7141 is a UV-curable adhesive with a secondary anaerobic cure mechanism. This makes it ideal for bonding materials such as ceramic-coated glass, mirrors, etc. where UV-light cannot penet.. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 100 °C |
47.2 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
Manifattura Cattaneo PA 6 Nylon Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 100 °C |
47.2 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
Manifattura Cattaneo PET+PTFE Polyethylene Terephthalate Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 20.0 °C |
47.2 µin/in-°F @Temperature 68.0 °F |
DIN 53752 |
GEHR Plastics PA 6 Nylon 6, Dry Polyamide shows both a high thermostability and high stiffness, hardness and toughness. These are some of the main characteristics. Due to the fact, that the good mechanical characteristics will be .. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-2:1999 |
Global EPP PA 6E Extruded Polyamide 6 Polyamides, commonly referred to as nylons, are macromolecular, partially crystalline thermoplastics. Their physical properties are mainly determined by the composition and structure of their molecu.. |
|||
CTE, linear | 85.0 µm/m-°C | 47.2 µin/in-°F | Alpha 2 |
Lord Adhesives Thermosetâ„¢ ME-525 Underfill Encapsulant LORD Thermosetâ„¢ ME-525 encapsulant is a high purity, semiconductor grade epoxy underfill product developed for the encapsulation of flip chip devices. It is formulated to reduce warpage and wit.. |
|||
CTE, linear | 85.0 µm/m-°C | 47.2 µin/in-°F | Alpha 2 |
Lord Adhesives Thermosetâ„¢ ME-531 Underfill Encapsulant LORD Thermosetâ„¢ ME-531 encapsulant is a high purity, semiconductor grade epoxy underfill product developed for the encapsulation of flip chip devices. It is formulated to reduce warpage and wit.. |
|||
CTE, linear | 85.0 µm/m-°C | 47.2 µin/in-°F | DIN 52328 |
Isoflon PA 6.6 Polyamide 6.6 General use for mechanical partsGood heat resistanceEasy to useHigh moisture regainInformation provided by Isoflon. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-2:1999 |
Global EPP PA 612 Copolymer Cast Polyamide 612 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
47.2 µin/in-°F @Temperature -22.0 - 176 °F |
ASTM E228 |
LyondellBasell DEXFLEX® 940 TPO Description: DEXFLEX® 940 is a thermoplastic olefinic elastomer (TPO) designed for large automotive exterior painted applications. Applications: Bumper fascias, claddings Information provided by .. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 20.0 °C |
47.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Styron INSPIREâ„¢ TF1500 ESU Polypropylene Talc filled, high impact PP compound. INSPIREâ„¢ TF1500 ESU has been developed for aesthetic automotive applications, with good scratch resistance and UV light stabilization.Information provided.. |
|||
CTE, linear | <= 85.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
<= 47.2 µin/in-°F @Temperature -22.0 - 176 °F |
Borealis Method |
Borealis Daplen™ EE115T TPO Compound Daplen EE115T is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE115T is a material with excellent impact /stiffness ratio. Thanks to its low th.. |
|||
CTE, linear | <= 85.0 µm/m-°C @Temperature 100 °C |
<= 47.2 µin/in-°F @Temperature 212 °F |
Borealis Test |
Borealis Daplen™ EE015U TPO Compound Daplen EE015U is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE015U is a material with excellent impact /stiffness ratio. Thanks to its low th.. |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6000 CP Nylon 6, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6000 HWUVCP Nylon 6, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6000 SCP Nylon 6, Finely Crystalline, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6000 SUVCP Nylon 6, Finely Crystalline, UV Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6600 HW Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6600 HWS Nylon 66, Finely Crystalline, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6600 HWUVCP Nylon 66, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6600 PA-66-HWL UL-Licensed Nylon 66, Flame Protection Grade V-2, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6600 PA-66-HWV0CP UL-Licensed Nylon 66, Flame Protection, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
CP-Polymer-Technik Wellamid® 6600 HWCP Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
CTE, linear | 85.0 µm/m-°C | 47.2 µin/in-°F | DIN 52328 |
Isoflon PA 6 Polyamide 6 General use for mechanical partsGood heat resistanceEasy to useHigh moisture regainInformation provided by Isoflon. |