Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 14.0 µm/m-°C @Temperature -40.0 - 125 °C |
7.78 µin/in-°F @Temperature -40.0 - 257 °F |
IPC-TM-650.2.4.41 |
Park Electrochemical Nelco® N5000-30/32 BT Epoxy Package The Nelco N5000-30 prepreg and N5000-32 laminate BT epoxy materials are designed specifically to meet or exceed new and emerging chippackaging requirements. The primary applications of these materia.. |
|||
CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | ASTM D696 |
Solvay Specialty Polymers Torlon® 4645 Polyamide-imide (PAI)
(Unverified Data**) Torlon 4645, an injection-moldable, wear-resistant grade of polyamide-imide (PAI), has been formulated to give outstanding wear resistance in lubricated wear applications. Torlon PAI has the highest.. |
|||
CTE, linear | 14.0 - 250 µm/m-°C | 7.78 - 139 µin/in-°F | Average value: 107 µm/m-°C Grade Count:46 |
Overview of materials for Polytetrafluoroethylene (PTFE), Molded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Molded". Each property range of values reported is minimum and maximum v.. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 °C |
7.78 µin/in-°F @Temperature 68.0 °F |
|
Cookson Group Plaskon® SMT-B-1LV Epoxy Molding Compound for PBGAs
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.An epoxy molding compound optimized specifically for grid arrays (BGA/LGA). Using an improved optimized filler system, it provide.. |
|||
CTE, linear | 14.0 - 47.0 µm/m-°C | 7.78 - 26.1 µin/in-°F | Average value: 23.4 µm/m-°C Grade Count:5 |
Overview of materials for Nylon 66/Nylon 6 Blend, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/Nylon 6 Blend, Glass Fiber Filled". Each property range of values reported is minimum and maxim.. |
|||
CTE, linear | 14.0 - 80.0 µm/m-°C | 7.78 - 44.4 µin/in-°F | Average value: 25.5 µm/m-°C Grade Count:29 |
Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Carbon Fiber/PTFE Filled". Each property range of values reported is minimum and maximum value.. |
|||
CTE, linear | 14.0 - 500 µm/m-°C @Temperature 55.0 - 160 °C |
7.78 - 278 µin/in-°F @Temperature 131 - 320 °F |
Average value: 154 µm/m-°C Grade Count:6 |
Overview of materials for Nylon 612, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Glass Fiber Filler". Each property range of values reported is minimum and maximum values of .. |
|||
CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | DIN 53752 |
Lehmann & Voss LUVOCOM® 1106-7843 Polyether imide, with glass fiber, PTFE, lubricant modified, easy flowing Applications: Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Information provided by Lehmann & Voss & Co.KG |
|||
CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | DIN 53752 |
Lehmann & Voss LUVOCOM® 1301/CF/20 PPS, linear, with carbon fiber Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts w.. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 200 °C |
7.78 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Nickel Strip - Alloy 360 Hard, 1.5 hr at 950°F Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: 1.5 hrs @ 510ºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation.. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 200 °C |
7.78 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Nickel Strip - Alloy 360 MH6, Mill Hardened Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation afte.. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 200 °C |
7.78 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H925 (H925) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011. |
|||
CTE, linear | 14.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C |
7.78 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F |
x-axis; IPC-TM 650-2.4.24 |
Industrial Laminates/Norplex NP347 Cotton Fabric Description: Bleached canvas with high temperature phenolic resin with molybdenum disulfide lubricant. Low moisture absorption. Capable of 150°C continuous operation.Thickness Tested: 0.062", 0.1.. |
|||
CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® SMC 0520 Unsaturated Polyester UP SMC 0520 is a special SMC with significantly reduced density. The glass level has been selected to combine good moulding with sufficient strength and stiffness properties. Even without a specific fi.. |
|||
CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | DIN 53752 |
Lehmann & Voss LUVOCOM® 1/CF/30 Polyamide 66, with carbon fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp.. |
|||
CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | DIN 53752 |
Lehmann & Voss LUVOCOM® 1/XCF/40 Polyamide 66, with carbon fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp.. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 200 °C |
7.78 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Nickel Strip - Alloy 360 Annealed Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedFormability Ratio, 90° Bend, Radius/Thickness (Good Way): 0Formability Ratio (bad Way): .. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 200 °C |
7.78 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Nickel Strip - Alloy 360 Annealed, 2.5 hr at 950°F Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: 2.5 hrs @ 510ºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation.. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 °C |
7.78 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Lubrizol Isoplast® 101LGF40NAT Engineering Thermoplastic Polyurethane Resin Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 °C |
7.78 µin/in-°F @Temperature 68.0 °F |
|
Williams Advanced Alloys WS217 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 100 °C |
7.78 µin/in-°F @Temperature 68.0 - 212 °F |
|
Goodfellow Nichrome®, Tophet A® Nickel 80 Chromium 20 Alloy Information provided by Goodfellow. |
|||
CTE, linear | 14.0 - 16.0 µm/m-°C | 7.78 - 8.89 µin/in-°F | |
Master Bond Supreme 11AN Two Component, Heat Resistant Epoxy Adhesive Description: Master Bond Polymer Adhesive System Supreme 11AN is a two component thermally conductive heat resistant epoxy adhesive with a one-to-one mix ratio, by weight or volume. It readily devel.. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 °C |
7.78 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Covestro Baydur® STR/C-400 BB Polyurethane Composite SRIM Foam, 60% Glass Filled, MDI-based 2-Component Liquid System Contains directed chopped fiber preform glass.0.16 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bay.. |
|||
CTE, linear | 14.0 - 16.0 µm/m-°C | 7.78 - 8.89 µin/in-°F | IPC TM-650 2.4.41 |
Arlon 49N Multifunctional Epoxy Low-Flow Prepreg 49N is a low-flow epoxy prepreg engineered for bonding multilayer epoxy rigid-flex or attaching heat sinks to multilayer PCBs. With a high Tg, the prepreg can be used in high-performance or high-te.. |
|||
CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | IPC TM-650 2.4.41 |
Arlon 51N Lead-Free Compatible Epoxy Low-Flow 51N is a non-DICY multifunctional epoxy low-flow prepreg system designed to provide high reliability through lead-free solder operations. The high decomposition temperature and high thermal stabili.. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 200 °C |
7.78 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H1050 (H1050) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011. |
|||
CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 200 °C |
7.78 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H775 (H775) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011. |
|||
CTE, linear | 14.0 - 16.0 µm/m-°C | 7.78 - 8.89 µin/in-°F | IPC TM-650 2.4.41 |
Arlon 44N Multifunctional Microdispersed Ceramic Filled Epoxy-Fiberglass Prepreg Arlon 44N is a high resin content multifunctional (175°C) epoxy prepreg system with a proprietary microdispersed ceramic filler system. 44N is engineered for the filling of clearance holes in thi.. |