Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
CTE, linear 40.0 - 130 µm/m-°C
22.2 - 72.2 µin/in-°F
Average value: 99.8 µm/m-°C Grade Count:22
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an..
CTE, linear 0.920 - 130 µm/m-°C
0.511 - 72.0 µin/in-°F
Average value: 102 µm/m-°C Grade Count:66
Overview of materials for Acetal Homopolymer, Unreinforced
This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced". Each property range of values reported is minimum and maximum values ..
CTE, linear 100 - 130 µm/m-°C
55.6 - 72.2 µin/in-°F
Average value: 120 µm/m-°C Grade Count:28
Overview of materials for Acetal Homopolymer, Unreinforced, Impact Grade
This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced, Impact Grade". Each property range of values reported is minimum and m..
CTE, linear 110 - 130 µm/m-°C

@Temperature 20.0 °C
61.1 - 72.2 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Kolon Kocetal® EC701 Modified Grade Acetal Copolymer  (discontinued **)
Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ..
CTE, linear 110 - 130 µm/m-°C

@Temperature 20.0 °C
61.1 - 72.2 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Kolon Kocetal® DP301 Modified Grade Acetal Copolymer  (discontinued **)
Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ..
CTE, linear 110 - 130 µm/m-°C

@Temperature 20.0 °C
61.1 - 72.2 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Kolon Kocetal® VT701 Modified Grade Acetal Copolymer  (discontinued **)
Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ..
CTE, linear 40.0 - 130 µm/m-°C
22.2 - 72.2 µin/in-°F
Average value: 87.5 µm/m-°C Grade Count:15
Overview of materials for Ethylene Vinyl Alcohol (EVOH)
This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Alcohol". Each property range of values reported is minimum and maximum values of appropr..
CTE, linear 110 - 130 µm/m-°C

@Temperature 100 - 100 °C
61.1 - 72.2 µin/in-°F

@Temperature 212 - 212 °F
Average value: 120 µm/m-°C Grade Count:3
Overview of materials for Ethylene Vinyl Alcohol (EVOH)
This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Alcohol". Each property range of values reported is minimum and maximum values of appropr..
CTE, linear 70.0 - 130 µm/m-°C

@Temperature 30.0 - 300 °C
38.9 - 72.2 µin/in-°F

@Temperature 86.0 - 572 °F
Average value: 100 µm/m-°C Grade Count:2
Overview of materials for Polytetrafluoroethylene (PTFE), Bronze Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Bronze Filled". Each property range of values reported is minimum and ma..
CTE, linear 94.0 - 130 µm/m-°C
52.2 - 72.2 µin/in-°F
Average value: 108 µm/m-°C Grade Count:6
Overview of materials for Fluorocarbon ETFE/ECTFE, Molded/Extruded
This property data is a summary of similar materials in the MatWeb database for the category "Fluorocarbon ETFE/ECTFE, Molded/Extruded". Each property range of values reported is minimum and maximum..
CTE, linear 20.0 - 130 µm/m-°C
11.1 - 72.2 µin/in-°F
Average value: 57.4 µm/m-°C Grade Count:11
Overview of materials for Nylon 12, 20% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. ..
CTE, linear 110 - 130 µm/m-°C

@Temperature 20.0 °C
61.1 - 72.2 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Kolon Kocetal® K700 General Purpose Grade Acetal Copolymer
Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ..
CTE, linear 120 - 130 µm/m-°C
66.7 - 72.2 µin/in-°F
ASTM D696
Guarniflon PTFE G400 Polytetrafluoroethylene
A virgin PTFE with low coefficient of friction, excellent chemical inertness, non-adhesive surface, wide service temperature range, and excellent dielectric propertiesInformation provided by Guarnif..
CTE, linear 120 - 130 µm/m-°C
66.7 - 72.2 µin/in-°F
ASTM D696
Guarniflon PTFE G415 Polytetrafluoroethylene 25% Soft Carbon
PTFE G Standard Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high ..
CTE, linear 110 - 130 µm/m-°C
61.1 - 72.2 µin/in-°F
Master Bond EP21TDC-4 Two Component, Highly Flexible Epoxy System
Master Bond Polymer System EP21TDC-4 is a two component, flexible epoxy resin system for high performance bonding, sealing and coating. It is formulated to cure at ambient temperatures or more quick..
CTE, linear 110 - 130 µm/m-°C
61.1 - 72.2 µin/in-°F
Master Bond EP21TDC-4ND Two component, highly flexibilized epoxy for bonding, sealing and coating
Product Description: Master Bond EP21TDC-4ND is a two component, very flexible epoxy system for high performance bonding, sealing and coating with a non-drip consistency. It has a one to four mix ra..
CTE, linear 15.0 - 130 µm/m-°C

@Temperature >=143 °C
8.33 - 72.2 µin/in-°F

@Temperature >=289 °F
Average value: 66.2 µm/m-°C Grade Count:12
Overview of materials for Polyetheretherketone, Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum..
CTE, linear 120 - 130 µm/m-°C
66.7 - 72.2 µin/in-°F
ASTM D696
Guarniflon PTFE G412 Polytetrafluoroethylene 15% Graphite
PTFE G Standard Compound with graphite.Properties: Extremely low coefficient of friction. Fairly good compressive strength. Enhanced chemical resistance. Good wear resistance. Good thermal diss..
CTE, linear 110 - 130 µm/m-°C
61.1 - 72.2 µin/in-°F
ASTM D696
Guarniflon PTFE G403 Polytetrafluoroethylene 15% Glass Fiber
PTFE G Standard Compound with glass fiberProperties: Enhanced wear resistance. Enhanced chemical resistance (except for alkali and hydrofluoric acid).Applications: Valve seats, seals, bearings, re..
CTE, linear 16.2 - 130 µm/m-°C
9.00 - 72.2 µin/in-°F
Average value: 35.9 µm/m-°C Grade Count:17
Overview of materials for Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified". Each property range of values reported..