Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : CTE, linear = 11.1 µin/in-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
CTE, linear 10.0 - 20.0 µm/m-°C

@Temperature 50.0 - 100 °C
5.56 - 11.1 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Raschig Group 2567 AMC
Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and ..
CTE, linear 10.0 - 20.0 µm/m-°C

@Temperature 50.0 - 100 °C
5.56 - 11.1 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Raschig Group 2568 AMC
Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s..
CTE, linear 10.0 - 20.0 µm/m-°C

@Temperature 50.0 - 100 °C
5.56 - 11.1 µin/in-°F

@Temperature 122 - 212 °F
Injection; ISO 11359-2
Raschig Group 2572 AMC
Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin..
CTE, linear 15.0 - 20.0 µm/m-°C

@Temperature 50.0 - 150 °C
8.33 - 11.1 µin/in-°F

@Temperature 122 - 302 °F
ISO 11359-2
Raschig Group 3505 Epoxy
Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed..
CTE, linear 15.0 - 20.0 µm/m-°C

@Temperature 50.0 - 150 °C
8.33 - 11.1 µin/in-°F

@Temperature 122 - 302 °F
ISO 11359-2
Raschig Group 3535 Epoxy
Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack..
CTE, linear 15.0 - 20.0 µm/m-°C

@Temperature 50.0 - 150 °C
8.33 - 11.1 µin/in-°F

@Temperature 122 - 302 °F
ISO 11359-2
Raschig Group 3536 Epoxy
Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed..
CTE, linear 15.0 - 20.0 µm/m-°C

@Temperature 50.0 - 150 °C
8.33 - 11.1 µin/in-°F

@Temperature 122 - 302 °F
ISO 11359-2
Raschig Group EPOXIDUR® 3582 EP Epoxy
Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Moldi..
CTE, linear 10.0 - 20.0 µm/m-°C

@Temperature 50.0 - 100 °C
5.56 - 11.1 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Raschig Group RALUPOL® 4385 UP
Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy..
CTE, linear 10.0 - 20.0 µm/m-°C

@Temperature 50.0 - 100 °C
5.56 - 11.1 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Raschig Group RALUPOL® 4806 UP
Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80..
CTE, linear 10.0 - 20.0 µm/m-°C

@Temperature 50.0 - 100 °C
5.56 - 11.1 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Raschig Group RALUPOL® 8602 UP
Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng..
CTE, linear -4.00 - 20.0 µm/m-°C

@Temperature 55.0 - 260 °C
-2.22 - 11.1 µin/in-°F

@Temperature 131 - 500 °F
Average value: 8.00 µm/m-°C Grade Count:3
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max..
CTE, linear -4.00 - 20.0 µm/m-°C

@Thickness 2.00 - 4.00 mm
-2.22 - 11.1 µin/in-°F

@Thickness 0.0787 - 0.157 in
Average value: 8.00 µm/m-°C Grade Count:3
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max..
CTE, linear 20.0 - 20.0 µm/m-°C

@Temperature 100 - 200 °C
11.1 - 11.1 µin/in-°F

@Temperature 212 - 392 °F
Average value: 20.0 µm/m-°C Grade Count:1
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%..
CTE, linear 12.6 - 20.0 µm/m-°C
7.00 - 11.1 µin/in-°F
Average value: 17.1 µm/m-°C Grade Count:5
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl..
CTE, linear 15.0 - 20.0 µm/m-°C
8.33 - 11.1 µin/in-°F
VDE 0304T1
Bulk Molding Compounds tetra-DUR F 4209 Bulk Molding Compound
Highest Arc resistanceTypical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion protection), therm..
CTE, linear 16.2 - 20.0 µm/m-°C
9.00 - 11.1 µin/in-°F
Average value: 18.3 µm/m-°C Grade Count:7
Overview of materials for Polycarbonate, 40% Glass Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. E..
CTE, linear 20.0 - 20.0 µm/m-°C

@Temperature 160 - 249 °C
11.1 - 11.1 µin/in-°F

@Temperature 320 - 480 °F
Average value: 20.0 µm/m-°C Grade Count:1
Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are ..
CTE, linear 12.0 - 20.0 µm/m-°C
6.67 - 11.1 µin/in-°F
VDE 0304T1
Bulk Molding Compounds tetra-DUR N 4203 Bulk Molding Compound
Highest dimensional stability under temp. Low profile.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipat..