Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 90.0 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 55.0 - 90.0 °C
131 - 194 °F
Average value: 65.1 °C Grade Count:13
Overview of materials for PETG Copolyester
This property data is a summary of similar materials in the MatWeb database for the category "PETG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M..
Deflection Temperature at 1.8 MPa (264 psi) 80.0 - 90.0 °C
176 - 194 °F
TMA
Solvay Specialty Polymers Hylar® 460 PVDF Polyvinylidene Fluoride  (discontinued **)
Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In a..
Deflection Temperature at 1.8 MPa (264 psi) 85.0 - 90.0 °C
185 - 194 °F
ASTM D648-98c
DSM Somos® NanoTool™ Resin for Stereolithography, UV Postcure
DescriptionNanoTool produces strong, stiff, high temperature resistant composite parts on conventional stereolithography machines. This third generation of Somos® ProtoComposite materials is heavi..
Deflection Temperature at 1.8 MPa (264 psi) 80.0 - 90.0 °C
176 - 194 °F
ASTM D648
Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion
Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a..
Deflection Temperature at 1.8 MPa (264 psi) 80.0 - 90.0 °C
176 - 194 °F
ASTM D648
Arkema Group KYNAR® 460 Red Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
Characteristics: Broad molecular weight distribution, pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, ..