Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C @Thickness 3.18 mm |
156 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Extrusion 84110 Polyvinyl Chloride, Rigid (PVC, Rigid) Note: NSF listings are obtained on specific colors. Contact PolyOne for the latest listing of approved colors for this product. Note: The Cell Classification was determined using the notched Izod te.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C @Thickness 3.18 mm |
156 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Extrusion L0152 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C @Thickness 3.18 mm |
156 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Extrusion L0248 Opaque Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C @Thickness 3.18 mm |
156 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Extrusion L0678 Natural Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C @Thickness 3.18 mm |
156 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Extrusion L1101 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
RheTech Products CC40P100-00 40% Calcium Carbonate Reinforced Polypropylene, Natural Applications: Consumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
Spartech PP5321 Mica Reinforced Homopolymer Information provided by Spartech |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | |
Aclo Accucomp Polyethylene HD0205L High Density |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | |
Aclo Accutech Polypropylene Homopolymer HP0336M20CL Mica Reinforced Coupled |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | |
Aclo Accutech Polypropylene Homopolymer HP0336M20L Mica Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
Asahi Kasei Thermylene® P6-16FG-0801 16% Fiber Glass Reinforced, UV Stabilized Information provided by Asahi Thermofil |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D-648 |
Axiall 7407 Rigid PVC, Extrusion Georgia Gulf 7407 is a rigid PVC compound designed for outdoor applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D-648 |
Axiall 7777 Rigid PVC, Extrusion Georgia Gulf 7777 is a rigid PVC compound designed for outdoor applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
RheTech Products CC40P100-01 40% Calcium Carbonate Reinforced Polypropylene, Black Applications: Consumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D-648 |
Axiall 5006 Rigid PVC, Extrusion, Natural Georgia Gulf 5006 Natural is a rigid PVC pellet compound designed for extrusion of interior rigid PVC profiles and various contours where high gloss and ease of processing is required. Georgia Gulf.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D-648 |
Axiall 5006 Rigid PVC, Extrusion, White Georgia Gulf 5006 White is a rigid PVC pellet compound designed for extrusion of rigid PVC house siding, window profiles and various contours where maximum weather resistance is required. Georgia G.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |
RheTech Products M20P100-01A 20% Mica Reinforced Polypropylene, Black Applications: Fan shroudsFiller panelsAir ductsInjection molding conditions reported in table.Information provided by RheTech Products. |