- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 56.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 56.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP FARADEX MS002 PP (Asia Pacific) LNP* Faradex* MS002 is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Faradex MS002P PP (Asia Pacific) LNP* Faradex* MS002P is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, Exceptional Processi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP FARADEX MS003 PP (Asia Pacific) LNP* Faradex* MS003 is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC 12000 Polypropylene Copolymer Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 - 200 °C | 133 - 392 °F | Average value: 108 °C Grade Count:10 |
| Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO 75 |
| LyondellBasell Hifaxâ„¢ BB222GC Thermoplastic Olefin Resin Key Features: medium melt flow, very high modulus, UV-stabilized thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, excellent weatherability, high stiffness, good dimens.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin (Europe-Africa-Middle East) Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP ML004 PP LNP* LUBRICOMP* ML004 is a product based on Polypropylene containing 20% PTFE. Added features of this grade include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 8620A PP SABIC® PPcompound 8620A is a mineral filled, impact modified polypropylene TPO. It was originally designed for painted automotive bumper fascia applications where a combination of good flow, hig.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT LNP* LUBRICOMP* WI001 is a compound based on PBT containing 2% Silicone. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DX99620C PC LNP STAT-KON* DX99620C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C @Thickness 3.20 mm |
133 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP WX05505 PBT LNP* Thermocomp* WX05505 is a compound based on Thermoplastic Polyester (PBT) resin containing proprietary fillers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermotuf PK005EI2 PA 6 (Europe-Africa-Middle East) LNP* THERMOTUF* PK005EI2 is a compound based on PA 6 resin containing Impact Modifier, Mineral. Added features include: High Impact.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ASTM D648 |
| A. Schulman POLYFORT™ FXP 3000-3120 Glass Sphere Filled Copolymer Polypropylene DescriptionPolyfort® FXP 3000-3120 is a 30% glass sphere filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO 75-93 |
| Wellman Wellamid® 22LHI6 XE-NBK1 Impact Modified Nylon 66 Description: Impact Modified Nylon 66Information provided by Wellman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO 75 |
| Unipetrol PP MONSTEN® GB 005 Polypropylene Homopolymer Applications include injection molding, tapes, and thermoforming. Basic stabilization. Homopolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Staramide R1000K PA66, Injection Molded Staramide R1000K is an Unreinforced Radiation Crosslinkable Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Staramide PK005EI2 PA6, Mineral Fiber Filled, Impact Modified Injection Molded Staramide PK005EI2 is an Impact Modified Mineral Filled Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ASTM Test |
| BASF Ultramid® 8350 HS PA6 (Dry) Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | |
| Arkema Group Rilsan® BESN G9 TL Nylon 11, Graphite Filled (Conditioned) Designation ISO 1874-PA11,EHLS,18-010,CD10Grade with graphite filler for tubes extrusion. Available color: steel gray. Light and heat stabilized.No need of lubricant. Low friction coefficient. Good .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ASTM D648 |
| Ashley Polymers Ashlene® 630BU Nylon 6 Black utility grade Nylon 6 for injection molding.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | |
| Plastcom SLOVALEN PQ 83 T 40 PP, 40% mineral filling FeaturesModified PP for injection moulding with the content of 40% mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 (Asia Pacific) LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 - 160 °C | 133 - 320 °F | Average value: 77.4 °C Grade Count:26 |
| Overview of materials for Polypropylene Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene Glass Bead Filled". Each property range of values reported is minimum and maximum values o.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 - 142 °C | 133 - 287 °F | Average value: 81.1 °C Grade Count:143 |
| Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ASTM D256 |
| Washington Penn PPC7UF0-Black Polypropylene, High Flow Copolymer Injection Molding Grade. Heat Stabilized. Meets Ford ESH-M4D293-B Spec.Data provided by Washington Penn Plastic Co., Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ASTM D648 |
| A. Schulman POLYFORT™ FXP 3000-3120 Glass Sphere Filled Copolymer Polypropylene DescriptionPolyfort® FXP 3000-3120 is a 30% glass sphere filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON MD000ISC PP LNP STAT-KON* MD000ISC is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Stat-kon MD000IU PP (Asia Pacific) LNP* Stat-kon* MD000IU is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact, UV Stabilized.This data wa.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ASTM-D648 |
| Braskem CP 284R HECO Polypropylene Heterophasic Copolymer CP 284R is a heterophasic copolymer designed for injection molding of pails and containers with excellent stiffness/impact strength balance. This resin also exhibits excellent productivity and proce.. |
|||