Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 504 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
ISO 75Af
Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, Dry as Molded &a
AMODEL® A-1340 HS is a 40% mineral/glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, high tensile strength and low warpage..
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP OCL36AXP PPS (Europe-Africa-Middle East)
LNP* LUBRICOMP* OCL36AXP is a compound based on PPS-Branched resin containing Carbon Fiber, PTFE. Added features include: Electrically Conductive, Internally Lubricated.
Deflection Temperature at 1.8 MPa (264 psi) 262 °C

@Thickness 3.20 mm
504 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP UX96507 PPA
LNP* LUBRICOMP* UX96507 is a compound based on PPA containing proprietary fillers. Added feature of this grade is: Wear Resistant.
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Stat-kon OEL36A PPS
LNP* Stat-Kon* OEL36A is a compound based on Polyphenylene Sulfide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This ..
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-KON OEL36A PPS - BRANCHED
LNP* STAT-KON* OEL36A is a compound based on PPS - Branched resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 262 °C

@Thickness 3.20 mm
504 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON OEL36A PPS (Asia Pacific)
LNP* Stat-kon* OEL36A is a compound based on Polyphenylene Sulfide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
GB/T 1634.2-2004
Sichuan Deyang Haton® hGR31M1 Polyphenylene Sulfide
Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD
Deflection Temperature at 1.8 MPa (264 psi) 262 °C

@Thickness 3.20 mm
504 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP UCF22S PPA
LNP* Thermocomp* UCF22S is a compound based on Polyphthalamide resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Heat Stabilized, Electrically Conductive..
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend
LNP THERMOCOMP* ZF406XXX is a compound based on PPO Blend resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend (Asia Pacific)
LNP THERMOCOMP* ZF406XXX is a compound based on PPO Blend resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant.
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-KON OE004AE PPS - Branched
LNP STAT-KON* OE004AE is a compound based on PPS - Branched resin containing 20% Carbon Fiber. Added features of this material are: Easy Molding, Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON RV00AEXP PA 66 (Europe-Africa-Middle East)
LNP* VERTON* RV00AEXP is a compound based on PA 66 resin containing Long Glass Fiber.
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON RV00ASXP PA 66 (Europe-Africa-Middle East)
LNP* VERTON* RV00ASXP is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
DAM; ISO 75-1/-2
DuPont Performance Polymers Zytel® HTN 51G35HSLR BK420 Polyphthalamide (PPA)  (Unverified Data**)
35% Glass Reinforced PPA High Performance Polyamide Zytel HTN51G35HSLR BK420 is a 35% glass reinforced heat stabilized lubricated high performance polyamide resin with improved hydrolysis resistance..
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
DAM; ISO 75-1/-2
DuPont Performance Polymers Zytel® HTN LT51G35HSLR BL661A Polyphthalamide (PPA)  (Unverified Data**)
35% Glass Reinforced Laser Weldable PPA High Performance Polyamide Information provided by DuPont Performance Polymers
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON RV00ASXS PA 66 (Europe-Africa-Middle East)
LNP* VERTON* RV00ASXS is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Heat Stabilized
Deflection Temperature at 1.8 MPa (264 psi) 262 °C
504 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON RV00AXX9 PA 66 (Europe-Africa-Middle East)
LNP* VERTON* RV00AXX9 is a compound based on PA 66 resin containing Long Glass Fiber.
Copyright © lookpolymers.com All Rights Reserved